Yg8/ K20 Od48ID20L20mm 8% Co Tungsten Carbide Wear-Resisting Seat Rings

China Yg8/K20 Od48*ID20*L20mm 8% Co Tungsten Carbide Wear-Resisting Seat Rings, Find details about China Cemented Carbide Rings, Carbide Alloy Rings from Yg8/K20 Od48*ID20*L20mm 8% Co Tungsten Carbide Wear-Resisting Seat Rings

Basic Info.

Model NO.

YG8 OD48*ID20*L20mm

Grade

Yg8

Hardness

89.5hra

Density

14.8g/cm3

T.R.S

2600MPa

Usage

as Wear-Resistance

Outdiameter

48mm

Inner Diameter

20mm

Thickness

20mm

Surface

Only Sintered

Trademark

ZZUP

Transport Package

25kg. Carton

Specification

OD48*ID20*L20mm

Origin

Zhuzhou, Hunan, China

HS Code

820900100

Model NO.

YG8 OD48*ID20*L20mm

Grade

Yg8

Hardness

89.5hra

Density

14.8g/cm3

T.R.S

2600MPa

Usage

as Wear-Resistance

Outdiameter

48mm

Inner Diameter

20mm

Thickness

20mm

Surface

Only Sintered

Trademark

ZZUP

Transport Package

25kg. Carton

Specification

OD48*ID20*L20mm

Origin

Zhuzhou, Hunan, China

HS Code

820900100

Product Desciption

YG8/K20 OD48*ID20*L20mm 8% Co tungsten carbide wear-resisting seat rings
YG8/K20 OD48*ID20*L20mm 8% Co tungsten carbide wear-resisting seat rings

Specifications

1. Grade: YG8 , 8% Co
2. YG8,YG6,YG3,YG10,YG15,YT14,YT5,YT05,YT15,YG20,YG25,YL10.2,YS2T,YG6X etc all kinds of grades for your choose.
3. Can product customize drawing,sizes and shape.

Products Show

Grades choosing
Common grades for all kinds metal

Grade	Density g/cm3	Hardnes HRA	T.R.S Mpa	Performance&application recommended
YG6A	14.85	92.5	2000	Fine grain alloy,good wear resistance.it is suitable for manufacturing forming cutter,wear-resistant parts etc.
YG8	14.7	89.8	2800	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG11	14.4	88.5	2900	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG15	14.0	87.0	3000	Suitable for manufacturing punching dies, wear-resistant parts.
YG20	13.5	85.5	2800	High bending strength,suitable for manufacturing progressive dies and other punching dies.
YG25	13.1	81.5	2950	High bending strength,wear resistance lower than YM6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YS2T	14.25	92.0	2500	Fine grain alloy, with high wear resistance, bending strength, bonding resistance and thermal strength. it is suitable for machining refractory alloys,stainless steel, high manganese steel, etc.

Grades for cold mill roll or hot mill roll steel

Grade	Wc (%)	Co (%)	Ni (%)	Cr (%)	Density g/cm3	Hardness ≥HRA	T.R.S ≥Nmm2	Compression Strength ≥Nmm2	Thermal Expansivity 10-6/K	Thermal Conductivity W/cm.k	Young's Elastic Modulus KN/mm2
YGR60	70		30		12.8	78	2200	2900	7
YGR55	76		24		13.1	80	2400	3000	6.8	0.17	420
YGR45	80		20		13.5	81	2500	3100	6.4	0.14	480
YGR40	82		18		13.7	82.5	2600	3200	6.2	0.2	530
YGR30	85		15		14.2	84.8	2700	3300	6.1	0.2	530
YGR25	88		12		14.3	85	2600	3400	6	0.2	550
YGH55	74	26			12.9	80	2200	3000	7	0.17	450
YGH45	75	25			13.4	82	2400	3100	6.5	0.18	480
YGH40	82	18			13.6	83.5	2500	3200	6.4	0.19	500
YGH30	85	15			13.9	83.5	2400	3300	6.1	0.2	540
YGH25	88	12			14.1	85	2300	3400	6	0.2	560

Other grades and sizes can be offered as per customers' requirements

Common sizes:

Outdiameter (mm)	Inner diameter (mm)	Height (mm)	Outdiameter (mm)	Inner diameter (mm)	Height (mm)
90	51	4~100	125	45	4~100
90	20		125	80
90	3		130	40
95	75		130	50
95	68.5		140	90
95	74		142	78
100	65		150	90
100	62.1		210	200
100	20		161	108
105	46		212	120
105	65.5		158.8	87.32
105	81		170.66	95
105	75		180	87.32
110	20		180	120.65
110	30		228.3	126
110	90		208	126
114	94		228	130
115	65		285	160
115	60		320	260
120	46		280	240
120	65		318	280
120	60		600	550
125	45		800	200