Two Part Methacrylate Adhesive MMA for Composite Tailgate Bonding ( PT805 )
China Two Part Methacrylate Adhesive MMA for Composite Tailgate Bonding (PT805), Find details about China Acrylic Adhesive, Polyurethane Sealant from Two Part Methacrylate Adhesive MMA for Composite Tailgate Bonding (PT805)
Basic Info.
Model NO.
PT805
Characteristic
Durablility
Composition
Organic Material
Color
Grey
Color After Mixing
Grey
Density (Resin)
0.9 G/Cm^3
Density (Hardener)
1.08 G/Cm^3
Mix Ratio
10:1 by Volume
Work Time
4-6 Min
Full Cure Time
24 H
Temperature for Application
5 - 30 ºC
Operating Temperature
-40ºC~120ºC
Trademark
Secubond
Transport Package
50ml or 490 Ml One Set
Specification
ISO9001, ISO14001
Origin
China
HS Code
3506100090
Model NO.
PT805
Characteristic
Durablility
Composition
Organic Material
Color
Grey
Color After Mixing
Grey
Density (Resin)
0.9 G/Cm^3
Density (Hardener)
1.08 G/Cm^3
Mix Ratio
10:1 by Volume
Work Time
4-6 Min
Full Cure Time
24 H
Temperature for Application
5 - 30 ºC
Operating Temperature
-40ºC~120ºC
Trademark
Secubond
Transport Package
50ml or 490 Ml One Set
Specification
ISO9001, ISO14001
Origin
China
HS Code
3506100090
Product Desciption
Description:
Comens Secubond PT805 is a third generation advanced fast cure two-part methacrylate metal-bonding adhesive. PT805 can bond most of the metal except copper without the need of primer in the case of simple surface treatment. The product can also be used to bond common engineering plastics.
Characteristics:
1.100% Curing
2.Surface does not need to be treated strictly
3.Working time 4-6min
4.Fast curing
5.Widely used in various metals and engineering plastics
6.Excellent Fatigue Resistance
7.High Strength
Uses:
Used to bond the following materials
Storage and Shelf Life:
The Comens Secubond PT805 is packaged in a 490 mL side-by-side double tube. The recommended storage temperature is 8-25ºCand the storage period is 12 months. Storage at 12ºC helps to extend the shelf life of the product. Long-term exposure to temperatures above 25 ºC will shorten the shelf life of the product.The initiator component decomposes rapidly above 35ºC to destroy product reactivity. Do not expose the product to high temperature storage. Recommended storage environment: ventilated, dry and dark.
Application Note:
It is recommended to use the 490mL 10:1 manual/pneumatic glue gun (Mixpac/NSJ)and mixing tube recommended by our company for sizing work.
Company Profile:
Production Base:
Automatic Production Lines and Quality Assurance:
Global Sales Network:
Certificates:
COMENS,A FULL RANGE OF SOLUTIONS
FOR MULTIPLE INDUSTRIES
Comens Secubond PT805 is a third generation advanced fast cure two-part methacrylate metal-bonding adhesive. PT805 can bond most of the metal except copper without the need of primer in the case of simple surface treatment. The product can also be used to bond common engineering plastics.
Characteristics:
1.100% Curing
2.Surface does not need to be treated strictly
3.Working time 4-6min
4.Fast curing
5.Widely used in various metals and engineering plastics
6.Excellent Fatigue Resistance
7.High Strength
Uses:
Used to bond the following materials
Metals: aluminum, cold rolled steel, magnesium alloy, stainless steel
Engineering Plastics: PC/ABS, ABS, acrylic resin, polycarbonate, PVC
Composite materials: epoxy, unsaturated polyester, vinyl ester and polyurethane.
Technical Data Sheet:
Note: the following information and data are typical values under standard conditions, not as basis for product acceptance. If the test environment is not explicitly mentioned in the following tests, the test environment is unified to a temperature of 24 ± 2ºC and a humidity of 50 ± 5% RH.
Note:
1. Working Time: Working Time: It refers to the time when the PT805 is mixed from the part A and B to the time when the adhesive is no longer useable on approximate 5mm beads. Times presented were tested at 24ºC.
2. Fixture Time: Varies with ambient temperature, bondline gap thickness, and nature of substrates. Typically at 24ºC, PT805 with 0.75mm gap reaches 500 psi in 18 minutes, and 1,000 psi in 19 minutes on Al 6061 . Substrate, temperature and gap may also affect fixture time(GBT 7124-2008).
Technical Data Sheet:
Note: the following information and data are typical values under standard conditions, not as basis for product acceptance. If the test environment is not explicitly mentioned in the following tests, the test environment is unified to a temperature of 24 ± 2ºC and a humidity of 50 ± 5% RH.
| Parameters | PT805 A | PT805 B | Mixture |
| Color | Off-White | Grey | Grey |
| Density/g/cm3 | 0.96 | 1.08 | 0.98 |
| Status | viscous glue | viscous glue | viscous glue |
| Viscosity/Pa.s | 100-130 | 20-60 | - |
| Working Time/min | - | - | 4-6/24ºC |
| Gap Filling/mm | 9 | ||
| Fixture Time /min | 18/24ºC | ||
| Full Cure Time/h | 24 | ||
| Operating Temperature | -40ºC~120ºC | ||
| Mix Ratio | A/B=10:1(Mix Ratio by Volume) A/B=8.89:1(Mix Ratio by Weight) | ||
1. Working Time: Working Time: It refers to the time when the PT805 is mixed from the part A and B to the time when the adhesive is no longer useable on approximate 5mm beads. Times presented were tested at 24ºC.
2. Fixture Time: Varies with ambient temperature, bondline gap thickness, and nature of substrates. Typically at 24ºC, PT805 with 0.75mm gap reaches 500 psi in 18 minutes, and 1,000 psi in 19 minutes on Al 6061 . Substrate, temperature and gap may also affect fixture time(GBT 7124-2008).
Storage and Shelf Life:
The Comens Secubond PT805 is packaged in a 490 mL side-by-side double tube. The recommended storage temperature is 8-25ºCand the storage period is 12 months. Storage at 12ºC helps to extend the shelf life of the product. Long-term exposure to temperatures above 25 ºC will shorten the shelf life of the product.The initiator component decomposes rapidly above 35ºC to destroy product reactivity. Do not expose the product to high temperature storage. Recommended storage environment: ventilated, dry and dark.
Application Note:
Although the Comens Secubond PT805 does not require special surface treatments and can even be bonded with oil, in order to achieve the desired bonding effect, it is recommended to clean the surface of the adherent substrate with dust and oil in the following manner:
Metal:Wipe once with acetone,Wipe once with alcohol
Plastic substrate:Wipe twice with alcohol
It is recommended to use the 490mL 10:1 manual/pneumatic glue gun (Mixpac/NSJ)and mixing tube recommended by our company for sizing work.
Company Profile:
Production Base:
Automatic Production Lines and Quality Assurance:
Global Sales Network:
Certificates:
COMENS,A FULL RANGE OF SOLUTIONS
FOR MULTIPLE INDUSTRIES
You Might Also Like
Best Selling 50kg High Quality Electronic Digital Hanging Ha......
Fuller Auxiliary Box High / Low Gear Synchronizer (A-5056) H......
Hydroponic Farm Fertilizer Tank pH/Ec Monitor Automatic Digi......
Industrial Motorized Electric Actuated Ball Valve Manufactur......
Halal and Kosher Cert No Shell Walnut Light Halves Walnut
Garlic Flavor Fried Fava Bean Chips with Brc
Block Making Machine Qt8- 15D Concrete Molds Block Brick Mac......
HS Code Heavy Duty ISO 17712 High Security Bolt Seal
Pen Drive 16GB OEM Nylon Rope USB Drives Lanyard Custom USB ......
LED Concert Scene Background LED Display Screen
330ml 500ml 1.5L Pet Water Bottle Blowing Making Machine
Buttons Laser Marking Machine (DW- F10W )