Structural Ms Polymer Composite Materials Bonding Glue Sealant for Automobile (Flexibond 8101t )

China Structural Ms Polymer Composite Materials Bonding Glue Sealant for Automobile (Flexibond 8101t), Find details about China Composite Glue, Polyurethane Adhesive from Structural Ms Polymer Composite Materials Bonding Glue Sealant for Automobile (Flexibond 8101t)

Basic Info.

Model NO.

Flexibond 8101T

Color

Grey

Curing Mechanism

Poly Reaction

Color After Mixing

Grey

Density (Resin)

1.25 G/Cm^3

Density (Hardener)

1.47 G/Cm^3

Mix Ratio

2:1

Application Time After Mixing

10-15 Min

Curing Condition (23ºC)

168 H

Electrophoresis

up to 230ºC

Tensile Strength

3.5 MPa

Shear Strength

2.5 MPa

Elongation at Break

450%

Trademark

Flexibond

Transport Package

400ml 2: 1 Jointed Cartridge Set

Specification

ISO9001, ISO14001

Origin

China

HS Code

3506100090

Model NO.

Flexibond 8101T

Color

Grey

Curing Mechanism

Poly Reaction

Color After Mixing

Grey

Density (Resin)

1.25 G/Cm^3

Density (Hardener)

1.47 G/Cm^3

Mix Ratio

2:1

Application Time After Mixing

10-15 Min

Curing Condition (23ºC)

168 H

Electrophoresis

up to 230ºC

Tensile Strength

3.5 MPa

Shear Strength

2.5 MPa

Elongation at Break

450%

Trademark

Flexibond

Transport Package

400ml 2: 1 Jointed Cartridge Set

Specification

ISO9001, ISO14001

Origin

China

HS Code

3506100090

Product Desciption

Description:
Flexibond 8101T is a two-component structural sealing MS polymer, which has excellent elongation, high bonding strength, and very good aging resistance under high temperature and humidity. 8101T is primer-less, has very good adhesion to various metal and non metal materials. It contains no volatile solvents, with non-sagging, moderate viscosity, fast curing and bonding effect. It also has good resistance for high temperature in short time, especially suits the needs for electronic coating processing.

Advantages:
Flexibond 8101T can be used for various metal and non metal materials bonding such as iron, aluminum, galvanized sheet, glass, fiberglass, PC, MSC, ABS, PVC etc. It can resist with 180ºC backing, in short time up to 230ºC. If used with our primer, it also can be used bonding with PE, PP.

.
Technical Data Sheet

Appearance	Grey
Solid content (%)	99.7%
	Modified Polymer
	ComponentA	ComponentB
Color	White uniform paste	Dark grey uniform paste
The color after mixing	Grey uniform paste
Density (before curing)	1.25g/cm3	1.47g/cm3
Mixing ratio (by volume)	100	50
Mixing ratio (by mass)	100	59
Application time after mixing (25ºC, 50%RH)	10-15mins
Curing Condition (23ºC)	168h
Tensile strength (25ºC, 50%RH)	3.5Mpa
Shear strength	2.5Mpa
Elongation at break	450%

Application:
The substrates should be clean and dry and of no grease, dust, or other contaminations. The substrates can be cleaned by alcohol or acetone. Polish is recommended if with aluminum and other difficult adhesion materials.

Put the cartridge into the manual or pneumatic applicator gun.
Remove the stopper at the top the cartridge, and screw the extrusion-type nozzle, and then cut the nozzle into a suitable shape and size according to your need.
Start the applicator gun and give up the sealant for the first 20cm, then apply to the substrates or the place for sealing.
Substrates have been coated with adhesive should be pressed within application time, ensure the fully coating of substrate, or the adhesion strength will be affected. Two or more workers are recommended
Replace with new nozzle If stop extrusion more than application time, make sure smooth processing
After application, put back the stopper with the left sealants, screw tight, sealing well
Must use with primer before application

Cleaning:
Recommended Cleaner: Acetone, butanone.

Packaging:
400ml 2:1 jointed cartridge set
200L metal drum
Production Base:
Structural Ms Polymer Composite Materials Bonding Glue Sealant for Automobile (Flexibond 8101t)