PTFE Bushes (SDRM50)

China PTFE Bushes (SDRM50), Find details about China Teflon Ptfe Tube, Various Fillers of Ptfe from PTFE Bushes (SDRM50)

Model NO.
SDRM50
Temperature
-180~+260 Degree
Tensile Strength(Min)
18mpa
Crack Elongation(Min)
230%
Productivity
100 Tons /Month
MOQ
50kgs
Trademark
Senrong
Specification
GB
Origin
Zibo, Shandong, China
HS Code
39172900
Model NO.
SDRM50
Temperature
-180~+260 Degree
Tensile Strength(Min)
18mpa
Crack Elongation(Min)
230%
Productivity
100 Tons /Month
MOQ
50kgs
Trademark
Senrong
Specification
GB
Origin
Zibo, Shandong, China
HS Code
39172900
Specification of molded:
1) ExterThickness 1-8mm
PTFE moulded PTFE pipe has advantage of good quality assurance and complete specifications. We have the most complete molds.

PTFE pipe is made by plunger extrusion of suspension polymerized PTFE resin. Among all the existing plastic, PTFE has the best corrosion-resistance and dielectricity.

Usage:
Lead insulating sleeve, corrosion-resistant pipe, and corrosion-resistant insulating pipe for different corrosive conditions, heat exchanger.

Main technical indicator:
1) Apparent density: 2.10 - 2.30g/cm3
2) Tensile strength (min): 18Mpa
3) Ultimate elongation (min): 230%

Specification of paste- extruded:
1) External diameter (mm): 0.5 - 4.0; Thickness (mm): 0.2 - 1.0; Length (mm): >=4, 000
2) External diameter (mm): 5.0 - 25.0; TThickness (mm): 1.0 - 25.0; Length (mm): . >=4, 000

Nal diameter (mm): 10 - 500
2) Thickness (mm): Thickness 1*-8mm
PTFE moulded PTFE pipe has advantage of good quality assurance and complete specifications. We have the most complete molds.

PTFE pipe is made by plunger extrusion of suspension polymerized PTFE resin. Among all the existing plastic, PTFE has the best corrosion-resistance and dielectricity.

Usage:
Lead insulating sleeve, corrosion-resistant pipe, and corrosion-resistant insulating pipe for different corrosive conditions, heat exchanger.

Main technical indicator:
1) Apparent density: 2.10 - 2.30g/cm3
2) Tensile strength (min): 18Mpa
3) Ultimate elongation (min): 230%

Specification of paste- extruded:
1) External diameter (mm): 0.5 - 4.0; Thickness (mm): 0.2 - 1.0; Length (mm): >=4, 000
2) External diameter (mm): 5.0 - 25.0; TThickness (mm): 1.0 - 25.0; Length (mm): >=4, 000

Specification of molded:
1) External diameter (mm): 10 - 500
2) Thickness (mm): >= 7
3) Length (mm): >=300

3) Length (mm): . >=300

Changed characters by filling Chemical substance:
(1)Glass Fiber: Increases compressive strength, rigidity and wear. Reduces creep and cold flow
Minimal effect on chemical and electrical properties
(2)Carbon: Increases compressive strength, hardness, wear, and load properties. Good chemical resistance. Various types and amounts of carbon can be added to alter conductivity
(3)Bronze: Increases hardness and wear resistance. Increases dimensional stability and compressive strength. Not suitable for corrosive or electrical applications
(4)Molybdenum Disulfide: Increases hardness, stiffness, and wear. Minimal effect on chemical and electrical properties
(5)Graphite: Reduces coefficient of friction. Reduces initial wear. Increases strength.
TYPES Specifications
  Outside diameter(mm) Wall thickness(mm) Length(mm)
Pressed pipe 1~25 0.1~2.5 Produced under requirements
Extruded pipe 25~200 1.5~8 Produced under requirements
Die pressed pipe 25~1200 5~500 100~300
 







Properties Unit Result
Apparent density g/cm ³ 2.10-2.30
Tensile strength(min) Mpa 18
Crack elongation (min) % 230