1-1.5mm Ceramic Bead Filled Wearing Compound

China 1-1.5mm Ceramic Bead Filled Wearing Compound, Find details about China Anti-Abrasive Epoxy Coating, Epoxy Coating with Ceramic Pearls from 1-1.5mm Ceramic Bead Filled Wearing Compound

Model NO.
215
Material
Epoxy
Classification
Room Curing
Main Agent Composition
Epoxy Resin
Characteristic
Waterproof
Promoter Composition
Curing Agent
Composition
Organic Material
Color
Grey
Package Available
500g, 5kg, 10kg, 20kg
Shelf Life
1 Year
OEM Service
Yes
Sample to Test
Yes
Trademark
Customized
Transport Package
5kg/Drum
Specification
500g/set
Origin
China
HS Code
3214109000
Model NO.
215
Material
Epoxy
Classification
Room Curing
Main Agent Composition
Epoxy Resin
Characteristic
Waterproof
Promoter Composition
Curing Agent
Composition
Organic Material
Color
Grey
Package Available
500g, 5kg, 10kg, 20kg
Shelf Life
1 Year
OEM Service
Yes
Sample to Test
Yes
Trademark
Customized
Transport Package
5kg/Drum
Specification
500g/set
Origin
China
HS Code
3214109000
TS215 Alumina Ceramic Minibead Filled Wear Compound

1-1.5mm Ceramic Bead Filled Wearing Compound1-1.5mm Ceramic Bead Filled Wearing Compound1-1.5mm Ceramic Bead Filled Wearing Compound

Product Description:

High-density, alumina ceramic bead-filled, toughened epoxy system for repairing and protecting equipment from wear and abrasion caused by handling and processing particulate matter as solid or in slurry form.

Product Features:
 

1.ceramic-filled for outstanding resistance to abrasion

2.Renews worn surfaces fast-reduces downtime

3.Extends wear life- resists sliding abrasive wear and eliminates costly wear part inventory

4.Non sag- provides abrasion resistance on over-head and vertical surfaces.



Product Application:

1.Cyclone and separator bodies

2.Dust collectors and exhausters

3.Pump liners and impellers

4.Fan blades and housings

5.Chutes and hoppers

6.Elbows and transition points


1-1.5mm Ceramic Bead Filled Wearing Compound1-1.5mm Ceramic Bead Filled Wearing Compound

Technical Data:
 

Color:

Black           

Specific gravity:

1.85g/cm³

Mix ratio by weight :

6:1

Mix ratio by volume:

4:1

Working time(min):

65min

Compressive strength(GB/T1041):125.0MPa
Tensile strength(GB/T6329):36.0MPa
Shear strength(GB/T7124):19.0MPa
Flexural strength(GB/T9341):75.0MPa

Fully cured time:

24h

Temperature range:

-60~150ºC


 

How to Use:

1. Surface treatment:
roughening the parts to be treated, sanding or sandblasting with an angle grinder, etc.; cleaning the roughened surface; the treated surface should be a rough and dry fresh substrate surface, and should be No oil and dust.
2. Preparation:
Mix the components A and B of the small particle wear-resistant protective agent according to the mass ratio A:B=4:1, and use them within 30 minutes.
3. Coating:
apply the uniformly mixed small particles of wear-resistant protective agent layer by layer to the area to be repaired, preferably at a thickness of 3-10 mm. The adhesive layer should be compacted to fully infiltrate the substrate; after the coating is applied to the required size, the surface layer is smoothed.
4. Curing:
Curing at 25ºC for 16 hours can be put into use. When the temperature is lower than 10 degrees, it can be cured by baking with an iodine tungsten lamp or electric heating plate for 2 hours.


Packing:

500g/set, 5kg/set, 10kg/set 


Transport and storage:

Keep the epoxy coating in dry, cool and covered facility, shelf life is 1 year. Avoid inversion and collision in transportation. This product is not dangerous goods.