Unsaturated Polyester Resin for Fiberglass, Fiberglass Ortho Resin

China Unsaturated Polyester Resin for Fiberglass, Fiberglass Ortho Resin, Find details about China up Resin, Unsaturated Polyester Resin from Unsaturated Polyester Resin for Fiberglass, Fiberglass Ortho Resin

Basic Info.

Model NO.

RESIN

Trademark

TIANMA

Specification

220kg/Drum

Origin

China

HS Code

39079100

Model NO.

RESIN

Trademark

TIANMA

Specification

220kg/Drum

Origin

China

HS Code

39079100

Product Desciption

TM-191RS UPR is a kind of general purpose use UPR, low viscosity, good mechanical strength and high elongation. It can be

applied in all kinds of FRP products as well as lay-up products.
2, Liquid resin technical data:

item	unit	index	test standard
Appearance	--	Clear pale yellow liquid	GB/T 8237.4.1.1
viscosity	25ºC, Pa.S	0.25~0.45	GB/T 7193.1
gel time	25ºC, min	9-17	GB/T 7193.6
acid value	mgKOH/g	25~30	GB/T 2895
non-volatile	%	61~67	GB/T 7193.3

Gel Time: 50% cyclohexano peroxide 4%, Accelerator E1: 4%:
3, resin casting matrix performance

item	unit	measured value	test standard
Barcol Hardness	--	41	GB 3854-83
HDT	ºC	70	GB 1634-04
Flexural Strength	MPa	114	GB/T 2570-95
tensile strength	MPa	60	GB/T 2568-95
Elongation at break	%	3.5	GB/T 2568-95
Impact Strength	KJ/m2	10.2	GB/T 2571-95

Remark: casting matrix should follow GB8237-87
Hardness system: hardener 55%MEKPO: 1.5% accelerator E1: 1%
60ºC× 3 Hours + 80ºC× 2 hours

The technical data of liquid resin:

1: Hand lay-up General purpose
Code	Type	25º C PA. S	Min	%	MPa	%	MPa	HDT	Application
		Viscosity	Gel time	Non-Volatile	Tensile	Elongation	Flexural
					Strength		Strength
TM-189	PA	0.25-0.45	10-22	59-65	60	4	100	57	Water resistance, for boat. CCS
TM-191	PA	0.25-0.45	9-17	61-67	55	1.8	110	66	Translucent, general FRP purpose
TM-191RS	PA	0.25-0.45	9-17	61-67	60	3.5	114	70	For FRP product, general purpose
TM-196	PA	0.60-1.20	9.1-18.9	64-70	76	2	120	72	Flexibility, high strength, CCS
TM-580	IPA	0.40-0.70	10-20	66-70	15	68	10	67	Flexibilizer or flexible resin, with other resins
TM-1032	PA	0.25-0.65	15-23	15-23	60	2	105	67	Good mechanical property, for bus, boat, CCS approval
TM-22	PA	0.34-0.38	16-22	16-22	62	2.3	108	65	Pre-promoted, thixotropy and low shrinkage
TM-2068	PA	0.20-0.40	11-25	11-25	58	1.5	110	100	Hot water resistance and high HDT, for bathtub
TM-10070	PA	0.30-0.34	8-18	8-18	65	2	115	68	Low viscosity, rapid wetting reinforcement for high strength FRP products.