China 10+12 Anti Wear Abrasion Steel Plate/Wearing Steel Plate, Find details about China Plate, Steel Plate from 10+12 Anti Wear Abrasion Steel Plate/Wearing Steel Plate
Our Wear plate has following advantages:
1. Flat surface and nice outlooking 2. Outstanding welding strength
3. Excellent wear resistance 4. Excellent impact resistance
5. Easy processing 6. High Cost Performance
7. Comprehensive quality control.
Other Feature and Property
Chemical composition: hardfacing overlay steel plate are manufactured by welding one or multiple abrasion resistant layers on Mild steel (Q235, Q345) or stainless steel (SS 304, SS 309, SS 310) base plate.
The overlay alloy has a high amount of chromium carbide hard particles.
Microstructure: The carbide (Cr7C3) volum fraction on the microstructure is above 50%.
Rockwell Hardness: Chromium carbide hard particles are distributed evenly throughout the layer, creating a strong microstructure,
The hardness is between HRC 57-62 and depend on the overlay's thickness: Overlay thickness over 10 mm. Hardness over 62 HRC.
Wear resistance: Our test shows that the Abrasion resistant performance of hardfacing overlay steel plate is 20 times higher than Mild steel and 8 times than heat treated steel.
Flatness tolerance: Flatness tolerance is ±3mm/m.
Thickness tolerance: Uniform overlay thickness, with tolerance within 0-0.3mm.
Product Name | Welldam Wear Resistant Steel |
Material | High chromium carbide overlay wear resistant steel |
Thickness | 4+4 5+3 6+4 6+5 8+4 8+6 8+8 10+4 10+6 10+8 10+10 12+4 12+6 12+8 12+10 14+6 14+8 14+10 16+6 16+8 16+10 16+12, etc. or as customized |
Weldable Thickness | 3-20mm |
Hardness | HRC 52-62 Wear deposite 3mm: HRC 52-58, 4mm: HRC 56-60, 5mm: HRC 58-62, 6mm: HRC 58-62, 8mm: HRC 58-62, 10mm: HRC 60-62, 12mm: >62 |
HRC of 1st layer :52-58; HRC of 2nd layer: 58-62; HRC of Pure weld deposite: 62 | |
Surface Treatment | Hardfacing clading coated. |
Technique | Advanced automatic self-shilded open arc welding |
Chemical Composition | Take 6+6 wear resistant steel for example: C : 4.3-4.8% Cr : 23-30% Mn : 0.8-1.1% Mo: 0.08-0.18 Ni:0.08-0.15 Other Metal elements : Micro |
Base Plate | Q235B, All weldable steels, mostly structural steels. |
Feature | High wear resistance 12-20 times higher than common plate 5-10 times than low alloy steel plate 2-3 times than high chromium cast iron plate |