Product Desciption

Polyethylene can be divided into high density polyethylene, low density polyethylene and linear low density polyethylene according to the polymerization method, molecular weight and chain structure.
LOW DENSITY POLYETHYLENE (LDPE), commonly known as high-pressure POLYETHYLENE, is mainly used in plastic bags and agricultural film due to its LOW DENSITY and the softest material.
HIGH DENSITY POLYETHYLENE (HDPE) is commonly known as low pressure POLYETHYLENE. Compared with LDPE and LLDPE, it has higher temperature resistance, oil resistance, steam permeability resistance and environmental stress cracking resistance. In addition, it has good electrical insulation, impact resistance and cold resistance, which is mainly used in blow molding and injection molding fields.
Linear Low Density Polyethylene (LLDPE) is a copolymer of ethylene and a small amount of advanced olefin in the presence of catalyst.LLDPE is similar to LDPE in appearance, with poor transparency and good surface gloss. LLDPE has the advantages of low temperature toughness, high modulus, bending resistance and stress cracking resistance, and good impact strength at low temperature.

1, LLDPE film grade
Tests	Value	Unit
Melt Flow Rate (MFR)	2.0±0.4	g/10min
Density	920±2	Kg/cm3
Tensile Strengthat Yield	8	Mpa ≥
Tensile Strengthat Break	12	Mpa ≥
haze	15	%≤
Packing	In 25 kg PP woven bags,20MT/20'FCL
2, LLDPE for Master Batch Use
Tests	Value	Unit
Melt Flow Rate (MFR)	20	g/10min
Density	0.924	g/cm3
Tensile Strength	MD12	Mpa
	TD 10
Elongation at Yield	13	%
Elongation at Break	200
Dark Drop Impact	105	g
Brittle Temperature(F 50)	-70	°C
Vicat Softening Point	90	°C
Packing	In 25 kg PP woven bags,20MT/20'FCL
3, LLDPE Powder Rotational Molding Grade for Tank Use
Tests	Value	Unit
Melt Flow Rate (MFR)	3.2	g/10min
Density	0.939	g/cm3
Melting Point	127	°C
Tensile Yield Strength	21	Mpa
Tensile Strength at Break	28	Mpa
Elongation at Break	1,100	%
Flexural Modulus	750	Mpa
Brittle Temperature	<-60	°C

4.Package&Storage&Transportation:

1.Packing:
   25kg/ carton or 25kg/bag, or per your requirement
   5kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container
2.Storage:
   The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air.
3.Transportation:
   During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil,       scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.