Products

3025 Phenolic Cotton Fabric Laminated Sheet/ Bakelite Sheet/ Micarta

China 3025 Phenolic Cotton Fabric Laminated Sheet/ Bakelite Sheet/ Micarta, Find details about China Insulation Material, Laminates from 3025 Phenolic Cotton Fabric Laminated Sheet/ Bakelite Sheet/ Micarta

Classification
Hybrid Insulation Materials
Certification
UL, ISO9001, IEC
Color
Brown
Trademark
Kang Liyuan
Transport Package
Pallet
Origin
China Mainland
Classification
Hybrid Insulation Materials
Certification
UL, ISO9001, IEC
Color
Brown
Trademark
Kang Liyuan
Transport Package
Pallet
Origin
China Mainland
3025 Phenolic cotton cloth laminate sheet
 
Heat-resistance: E CLASS 120C
Material: Cotton cloth and phenolic resin
Property: With high dielectric and mechanical property.
Application: With certain mechanical performance and electric performance for machine, motors and electrical apparatus, as well as transformer oil.
The specification:
Thickness(mm): 0.5-120mm
Size: 980X1980mm, 1020X2040mm, 1000X2000mm
Pacakge: PALLET Storage life---1 year
3025 Phenolic Cotton Fabric Laminated Sheet/ Bakelite Sheet/ Micarta
 
The technical requirements
NoPropertyUnitNormal value
1Flexural strength perpendicular to layer directionMPa≥ 100
2Impact strength parallel to the layer direction (Charpy method)kJ/m 2≥ 8.8
3Electrical strength perpendicular to the layer direction at 90± 2 ° C transformer oilMV/mRefer to table 3
4Breakdown voltage parallel to the layer direction at 90± 2 ° C transformer oilkV≥ 1
5Insulation resistance after immersing in waterMΩ≥ 1
6Water absorptionmgRefer to table 4
 

Tested Item		Unit
 		standard
 
Density  g/cm31.30-1.42
Martin temperature "vertical"ºC>=125
Vertical layer to bending strength "verticalMpa>=105
Tensile strength "vertical"Mpa>=65
Impact strength "beam method without gap samples, longitudinal
 		kJ/>=25
Bonding strengthN>=5400
Vertical layer to strength (90 ±2 ºC in transformer oil > 3mm, thickness, the side processing to 2.0 mm ±0.2 mm)MV/M>=2.0