China 0.50mm/0.75mm/1mm HDPE Geomembrane Liner, Find details about China HDPE Geomembrane, HDPE Liner from 0.50mm/0.75mm/1mm HDPE Geomembrane Liner
No. | Properties | Test Method | Test Value | |||||||
1 | Thickness(mm) | ASTM D5199 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 |
2 | Density (g/cm2) | ASTM D1505 | 0.939 | |||||||
3 | Tensile Propeties | |||||||||
Yield Strength(N/mm) | ASTM D6693 | 7 | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
Break Strength(N/mm) | 13 | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
Yield Elongation % | Type IV | 12 | ||||||||
Break Elongation % | 700 | |||||||||
4 | Tear Resistance/N | ASTM D1004 | 62 | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
5 | Puncture Resistance/N | ASTM D4833 | 160 | 240 | 320 | 400 | 480 | 640 | 800 | 960 |
6 | Stress Crack Tesistance/h | ASTM D5397 | 300 | |||||||
7 | Carbon Black | |||||||||
Carbon Black Content % | ASTM D1603 | 2.0-3.0 | ||||||||
Carbon Black Dispersion | ASTM D5596 | Carbon black dispersion for 10 different views 9 in categoried 1 or 2 and 1 in category | ||||||||
8 | Oxidative Induction Time(OIT) | |||||||||
Standard OIT/min | ASTM D3895 | 100 | ||||||||
High Pressure OIT/min | ASTM D5885 | 400 | ||||||||
9 | Oven Aging at 85°C | |||||||||
Standard OIT-% retained after 90 days | ASTM D3895 | 55 | ||||||||
High pressure OIT-% retained after 90 days | ASTM D5885 | 80 | ||||||||
10 | UV Resistance | |||||||||
Standard OIT retained after 1600 hrs | ASTM D3895 | 50 | ||||||||
High pressure OIT retained after 1600 hrs | ASTM D5885 | 50 | ||||||||
11 | Low tempreture impact brittle property at -70°C | _ | Pass | |||||||
12 | Permeability g·cm/(cm2)·Pa | _ | ≤1.0×10-13 |