Stellite 6 Wire/Electrode/Rod Cobalt Based Material

China Stellite 6 Wire/Electrode/Rod Cobalt Based Material, Find details about China Electrode, Welding from Stellite 6 Wire/Electrode/Rod Cobalt Based Material

Model NO.
Stellite 6
Slag Characteristic
Alkaline
Welding Power
AC or DC+
Trademark
Ocean Welding
Transport Package
5kg/Box, 20kg/Carton
Origin
Zhejiang, China(Mainland)
Model NO.
Stellite 6
Slag Characteristic
Alkaline
Welding Power
AC or DC+
Trademark
Ocean Welding
Transport Package
5kg/Box, 20kg/Carton
Origin
Zhejiang, China(Mainland)
Stellite 6 Wire/Electrode/Rod Cobalt Based Material
is a titanium calcium type coating, surfacing electrode with cobalt chromium tungsten alloy cores, should adopt DCRP. Surfacing metal can keep good abrasion resistance and corrosion resistance at 650 degrees.

Applications:
used in the work of 650 degrees Celsius should be able to maintain good wear resistance and a certain degree of corrosion resistance of the occasion; for example, the high temperature and high pressure welding valve and hot shear knife, the impact of hot and cold staggered place.
Chemical Composition of the deposited metal
 CMnCrW
Standard0.7-1.4≤225-323-6
 SiFeCoOther element
Standard≤2≤5allowance≤4
Electrode specification and reference current (AC or DC+):
Diameter(mm)3.24.05.0
Length(mm)350350350
Current(A)120-160140-190150-210

Notes:
1: before welding electrode must be 150 degrees bake for 1 hours
2: according to the size of the tool and the type of parent material, must be preheated by 300-600 DEG C, should use small current short arc welding
3: after welding should be tempered at 600-700 DEG C after 1 hours and then cold or immediately put the workpiece into the dry and hot sand box or plant ash in the cold, so as not to crack.