China Flame Retardant Plugging Agent, Find details about China High Temperature Resist Silicone, Silicone Rubber from Flame Retardant Plugging Agent
Technical datasheets of rtv electronic potting silicon rubebr
model | HY-9055 | HY-9060 | HY-9300 | |
Before Curing | Appearence |
| ||
Viscosisty cP | ±500 | B: 3000±500 | A: 600±200 B: 1800±200 | |
Operating Perform ance | A:B(w/w) | 1:1 | 1:1 | 1:1 |
Mixing Ratio cP | 2000~3000 | 2500~3500 | 600~1000 | |
Pot life min | 120 | 120 | 3h | |
Curing time (25°C) min | 480 | 480 | 480 | |
Curing time (80°C)min°C)min | 20 | 20 | 20 | |
After Curing | Hardness(Shore (Shore A) | 55±5 | 60±5 | 0 |
Thermal conductivity w/mK | ≥0.8 | ≥0.8 | ≥0.2 | |
Absolute degree Of dielectric kv/mm | ≥25 | ≥25 | ≥25 | |
Permittivity kv/mm | 3.0~3.3 | 3.0~3.3 | 3.0~3.3 | |
Volume Resistanc Ω·cm | ≥1.0×1014 | ≥1.0×1014 | ≥1.0×1014 | |
Linear expansion coefficient m/mK | ≤2.2×10-4 | ≤2.2×10-4 | ≤2.2×10-4 | |
Flame Resistance | UL94V1 | UL94V0 | UL94V1 | |
Performance and applications oon rtv electronic potting silicon rubebr
HY9055 and HY9060 are the two-component electronic encapsulants with low viscosity with flame Resistance and thermal conductivity.
Using instruction on rtv electronic potting silicon rubebr
1. Pls put part A and part B in separate container
2. Weight Ratio: part A: part B = 1:1
3. Deaeration the mixture under 0.08 MPa for 5 minutes.