Scu6240/Cual11fe3 Aluminum Bronze

China Scu6240/Cual11fe3 Aluminum Bronze, Find details about China Ercual-A3, Welding Wire from Scu6240/Cual11fe3 Aluminum Bronze

Model NO.
SCu6240/CuAl11Fe3
Standard
GB/T
Size
1.6mm (1/16 Inch)
Spool Type
D 300
Wire Weight
15kg Each Spool
Wire Type
Solid Wire
Condition
Half Hard
Surface
Smoothly
Aws
A5.7 Ercual-A3
BS En14640
Cual11fe
Trademark
Allotech
Transport Package
15kg Each Spool
Specification
1.6mm
Origin
China
HS Code
7408220000
Model NO.
SCu6240/CuAl11Fe3
Standard
GB/T
Size
1.6mm (1/16 Inch)
Spool Type
D 300
Wire Weight
15kg Each Spool
Wire Type
Solid Wire
Condition
Half Hard
Surface
Smoothly
Aws
A5.7 Ercual-A3
BS En14640
Cual11fe
Trademark
Allotech
Transport Package
15kg Each Spool
Specification
1.6mm
Origin
China
HS Code
7408220000
Scu6240/Cual11fe3 Aluminum Bronze
NAME: Aluminum Bronze
Physical & Mechanical Properties: 

Solids-Temperature 1030°C   
Density7.6kg/dm³   
Elongation 20%    
Liquids-Temperature 1045°C    
Tensile Strength 621N/mm²   
Brinell Hardness 166HB

Packaging  

MIG

Diameter

0.8 - 2.0mm

Packaging

D100mm D200mm D300mm

Weight

1kg/5kg/12.5kg/13.6kg/15kg

0.030"-5/64"

2lb/10lb/27lb/ 30lb/33lb

TIG

Diameter

1.6 - 6.4mm

Length

457mm / 914mm

Packaging

5kg/box  25kg/box 10kg/plastic package

1/16" - 1/4"

18" / 36"

10lb/box  50lb/box  10kg/plastic package

Introduction & chemical composition:
Recommended for the joining and overlay welding of copper-aluminium alloy, aluminium coated steel and cast iron .It has been widely used in ship building, machery, and the chemical industry. Best for high overlay welding requirement for hardness,resistance to wear, abrasion, and erosion.
 

Standard

Class

Alloy

Cu

Al

Fe

Mn

Ni

P

Pb

Si

Sn

Zn

other

GB/T9460

SCu6240

CuAl11Fe3

bal.

10.0-

2.0-4.5

-

-

-

max

max

-

max

max

11.5

0.02

0.1

0.1

0.5

BS EN14640

Cu6240

CuAl11Fe

bal.

10.0-11.5

2.0-4.5

-

-

-

0.02

-

-

0.1

0.5

AWS A5.7

C62400

ERCuAl-A3

bal.

10.0-11.5

2.0-4.5

-

-

-

0.02

0.1

-

0.1

0.5