Linear low density polyethylene(LLDPE)
CAS No.: 9002-88-4
Type: Synthetic Resin and Plastics
Appearance: Transparent beads
Linear low density polyethylene(LLDPE)
Color: Transparent
Density: 0.915-0.940
Usage: Film
1. Specifications:
2. Property:
1. With high transparency, no discoloration, good self-adhesive, good retraction ratio, good tensile properties, 1 meter can be on 3-5 meters use.
2. Non-toxic, tear-resistant, anti-puncture, hot temperature endurable;
3. Water-proof, moisture-proof, dust-proof, anti-corrosion
4. This is Pallet Wrap Film(LLDPE Stretch Film) produced by three layer common extruding machine, it provide excellent protection for the surface of packed products. It can reduce packaging cost, its economical, labor saving, efficiency increasing. Its easy to use and remove, suitable for palletized packaging of products and transportation operation.
3. Application:
1. Pallet packaging, carton packaging, wrapping bulk goods, daily necessities packaging;
2. Applied to various fields, such as Electronics, buliding materials, chemicals, materials, automobile components, wire&cable, paper, bottle, can, hardware and electrical materials etc.
Advantage:
Good resistance to stretch strength, resistance to penetrating, ripstop and elongation, especially suitable for the film. Excellent rheological property or melted liquidity, few shearing sensitivity...
PROPERTY | UNIT | SPECIFICATION |
Melt Flow Index | g/10min | ≤1.0 |
Density | g/cm3 | ≤0.945 |
Tensile strength | Mpa | ≥14.0 |
Elongation at break | % | ≥600 |
Brittle temperature at low temperature | °C | ≤-76 |
ESCR ,FO | H | ≥500 |
Carbon Black dispersion | -- | -- |
Tensile strength after thermal aging | Mpa | ≥13 |
Elongation after thermal aging | % | ≥500 |
Dielectric strength | Mv/m | ≥25 |
Volume resistivity | Ω.m | ≥1*1014 |
change rate of tensile strength after weather aging environment of 0--1008h | % | ±25 |
change rate of elongation after weather aging environment of 0--1008h | % | ±25 |
change rate of tensile strength after weather aging environment of 504--1008h | % | ±15 |
change rate of elongation after weather aging environment of 504--1008h | % | ±15 |