2mm chopped carbon fibre was cut from high modulus high strength PAN carbon fiber filament which will treated by pre-oxidation under 200ºC to 300ºC,carbonization in high purity inert gas under 1000ºC to 1500ºC,graphitization under 2500ºC to 3000ºC,finally been finished by sizing.It is chemical stable,weakly conductive,self-lubricating,high temperature resistance,abrasion resistance,acid resistance,high strength and high modulus.so it is excellent reinforcing filler of composite products.It can be compound with resin,plastic,rubber and other materials to increase products' strength and wear resistance.Widely used in many fields,such as electronic chips,conductive plate,conductive flooring,electrical machinery,anti-static industry,defense industry,building insulation,friction materials and chemical.
SPECIFICATIONS:
| Model: | XGT3-702 |
| Carbon content(%): | >98 |
| Fiber type: | T300 |
| Filament diameter(um): | 7 |
| Fiber length(mm): | 2 |
| Tensile strength(MPa): | 3600-3850 |
| Tensile modulus(GPa): | 220-245 |
| Elongation(%): | 1.5 |
| Density(g/cm3): | 1.76 |
| Volume resistivity(Ωcm): | 1.5×10-³ |
APPLICATION FIELDS:
1.Reinforced rubber,modified plastics and resin: Polypropylene (PP),nylon (PA),polycarbonate resin (PC),phenol resin (PF),polytetrafluoroethylene resin (PTFE),polyimide resins (PI ),epoxy resin, silicone rubber, polyvinyl alcohol, unsaturated polyester resin;
2.Construction industry: carbon fiber reinforced cement, conductive coatings, anti-static floors;
3.Shielding materials: Manufacturing shield smoke, shielding curtain wall;
4.Insulation materials: carbon fiber reinforced preform and refractory bricks, carbon-fiber reinforced ceramic, etc;
5.New energy: used as conductive additives of positive or negative materials in nickel hydride and nickel cadmium battery;
6.Anti-static industry: coating, flooring, paint, ink, anti-static filter,
7.Aerospace: composite materials for parts of aircraft and satellite.
8.Civilian areas: sports equipment, transportation, sanitary equipment, kitchen appliances.
STORAGE:
The 2mm chopped carbon fibre should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.
PACKAGING:
1.Inner plastic film bags with carton,carton size:45*45*30cm,net weight:10.00kg.gross weight:11.00kg.
2.24 cartons per pallet,net weight:240.00kg,gross weight:280.00kg
SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 20pallets(each 240kg.two layers)be loaded into 20 feet container.total net weight is 4.8metric tons.
2.transportation by truck:for truck transportation,generally 10 pallets(each 240kg,one layer) be loaded into truck.
3.transportation by rail:for rail transportation,generally 20 pallets(each 240kg,two layer)be loaded into train's container.