S17400 AISI 630 steel plate
EN 1.4462 - 329 is a high alloy austenitic stainless steel with low carbon content. The grade is intended for use under severe corrosive conditions. The steel grade was originally developed to resist corrosion in dilute sulphuric acid. EN 1.4462 is fully austenitic, and is less sensitive to precipitation of ferrite and sigma phase than conventional austenitic grades with high molybdenum content. Due to the combination of relatively high contents of chromium, nickel, molybdenum and copper,   EN 1.4462 has good resistance to general corrosion, particulary in dilute sulphuric acid.  It is non-magnetic in the annealed condition but may become slightly magnetic as a result of cold-working or welding.
Design features  
⇒ Good resistance to uniform corrosion
⇒ Good resistance to pitting and crevice corrosion  
⇒ Very good resistance to stress corrosion cracking
⇒ Good resistance to intercrystalline corrosion
⇒ Good formability and weldability
Corrosion resistance  
Uniform corrosion Uniform corrosion is characterized by a uniform corrosion of the steel surface in contact with the corrosive medium. Resistance is normally considered good if the corrosion rate is less than 0,1 mm/year. As a result of its high chromium, nickel and molybdenum contents and its alloying with copper, EN 1.4462 is passivated even in reducing environments such as dilute sulphuric acid and formic acid. Its high nickel content contributes towards its relatively low corrosion rate in the active state.  
Intercrystalline corrosion  
EN 1.4462 has a very low carbon content. This means that there is very little risk of carbide precipitation in connection with ordinary heat treatment and welding. The risk of intercrystalline corrosion after ordinary heat treatment and welding is thereby eliminated.

Company Information:
Phone:+8613400008153
Tel: 0510-88222973
Fax: 0510-88222975
Web: taixie.en.made-in-china.com
Over 16 years of specialist experience in Copper, Mould steel, steel alloy! Welcome to order and customized.