China Alloy Steel Casting Series Round Ring and Individual Ring Sand Casting for Cement Industry, Find details about China Alloy Steel Casting, Pipe Fitting from Alloy Steel Casting Series Round Ring and Individual Ring Sand Casting for Cement Industry
| NO. | Chemical composition%% | Max temperatureºC | Yield Strength | Elongation%% | ||||||||||
| C | Mn | Si | Cr | Ni | P | S | Mo | W | N | |||||
| ZG30Cr24Ni7NRe | 0.32 | < | 1.3 | 23 | 7 | < | < | 0.22 | 1100 | |||||
| - | = | - | - | - | = | = | - | |||||||
| 0.42 | 2 | 2 | 25 | 8.5 | 0.035 | 0 | 0.3 | |||||||
| ZG40Cr25Ni35Mo | 0.35 | 1 | 1 | 24 | 34 | < | < | 1150 | 196 | 8 | ||||
| - | - | - | - | - | = | = | -20 | |||||||
| 0.45 | 2 | 1.8 | 27 | 36 | 0.04 | 0 | ||||||||
| ZG10Cr18Ni9Ti | < | 0.8 | < | 17 | 8 | < | < | 850 | ||||||
| = | - | = | - | - | = | = | ||||||||
| 0.12 | 2 | 1.5 | 20 | 11 | 0.04 | 0 | ||||||||
| ZG40Cr25Ni20Si2 | 0.35 | 1 | 1 | 23 | 19 | < | < | 1150 | 225.4 | 12 | 10 | |||
| - | - | - | - | - | = | = | -23 | |||||||
| 0.45 | 2 | 1.8 | 26 | 22 | 0.04 | 0 | ||||||||
| ZG40Cr28Ni48W5 | 0.4 | 1 | 1 | 27 | 47 | < | < | 4 | 1200 | 196 | 4 | |||
| - | - | = | - | - | = | = | - | -20 | ||||||
| 0.5 | 2 | 1.8 | 29 | 49 | 0.04 | 0 | 5.5 | |||||||
| ZG10Cr20Ni14Si2 | 0.35 | 1 | 1 | 19 | 13 | < | < | 900 | 240 | 25 | 10 | |||
| - | - | - | - | - | = | = | -24.5 | |||||||
| 0.45 | 2 | 1.8 | 21 | 15 | 0.04 | 0 | ||||||||
| ZG10Cr15Ni36W3Ti | < | 1 | < | 14 | 34 | < | < | 2.8 | 1 | 1160 | 40 | 15 | ||
| = | - | = | - | - | = | = | - | - | ||||||
| 0.12 | 2 | 0.8 | 16 | 38 | 0.035 | 0 | 3.2 | 1.4 | ||||||
| 10Cr18Ni9Ti | < | < | < | 17 | 8 | < | < | 55 | 40 | |||||
| = | = | = | - | - | = | = | ||||||||
| 0.12 | 2 | 1 | 19 | 11 | 0.035 | 0 | ||||||||
| 10Cr25Ni20Si2 | < | < | 1.5 | 24 | 18 | < | < | 60 | 35 | |||||
| = | = | - | - | - | = | = | ||||||||
| 0.2 | 1.5 | 2.5 | 27 | 21 | 0.035 | 0 | ||||||||
| 10Cr20Ni14Si2 | < | < | 1.5 | 19 | 12 | < | < | 60 | 35 | |||||
| = | = | = | - | - | = | = | ||||||||
| 0.2 | 1.5 | 2.5 | 22 | 15 | 0.035 | 0 | ||||||||