China Brass Sheet & Brass Plate with High Quality, Find details about China Brass Coil, Brass Plate from Brass Sheet & Brass Plate with High Quality
| 1. | standard: |
| 1). | meet the technical conditions GB/T 2059-2008 and GB17793-1999 standards. |
| 2). | Chemical ingredients meet the GB5232-2001 standard. |
| 3). | in accordance with ISO9001-2000 Quality system requirements |
| 4). | The special requirements will be satisfied when users have put forward. |
| 2. | Range of work: |
| 1). | thickness: 0.8--40mm |
| 2). | width: 400 or 600mm |
| 3). | length: max 2m |
| 3. | Range of usage: |
| 1). | transformer |
| 2). | water heater exchanger |
| 3). | automotive manufacturers |
| Element | Content(%) |
| Iron, Fe | ≤ 0.050 |
| Lead, Pb | ≤ 0.15 |
| Zinc, Zn | 37-39 |
| Copper, Cu | 62.0 |
Item | Specification | Characteristics | Application | |||
ASTM | DIN | JIS | GB | |||
C28000 | CuZn40 | C2800 | H62 | 0.3-12.0mm | Excellent cold plastic, elastic, high strength. | Fasteners, battery, driving screw, glasses fittings, electronic component ,connects, springs, zipper, craft accessories, wire electrode. |
C27400 | CuZn37 | C2720 | H63 | |||
C27000 | CuZn36 | C2700 | H65 | |||
C26800 | CuZn30 | - | H68 | |||
C26000 | CuZn30 | C2600 | H70 | |||
C24000 | CuZn20 | C2400 | H80 | |||
C23000 | CuZn15 | C2300 | H85 | |||
C22000 | CuZn10 | C2200 | H90 | |||
Item | SIZE | Characteristics | Usage | |||
ASTM | DIN | JIS | GB | |||
C36000 | CuZn36Pb3 | C3602 | HPb62-3 | 1.0-120mm | With excellent cutting, drilling performance, high strength, good conductivity and corrosion resistance. | Suitable for automatic lathes, CNC lathe processing products, such as hardware, electrical connectors, connector. |
- | - | C3603 | - | 1.0-120mm | ||
C37700 | CuZn39Pb2 | C3771 | HPb61-1 | 1.0-120mm | ||
C38000 | CuZn39Pb3 | C3604 | HPb60-2 | 1.0-120mm | ||
C38500 | CuZn40Pb3 | C3605 | HPb59-3 | 1.0-120mm | ||
C37000 | CuZn40Pb2 | C3710 | HPb59-1 | 1.0-120mm | ||
- | - | - | HPb58-3 | 1.0-120mm | ||
Item | Specification | Characteristics | Application | |||
ASTM | DIN | JIS | GB | |||
C67420 | CuZn37Mn3Al2PbSi(CW713R) | - | HMn59-2-2 | 5.0-120mm | Manganese brass with high strength, high wear resistance, corrosion resistance. | Widely used in auto, hydraulic pressure, machinery manufacturing industry. Main applications are auto synchronizer ring gear, turbocharger, bearings, shaft sleeve, gear. |
C67300 | - | - | - | |||
- | CuZn38Mn2NiSi | - | - | |||
C66800 | - | - | - | |||
C86300 | DIN1709 G-CuZn25Al5 | - | (HAl64-5-4) | 5.0-120mm | High hardness, high strength, high abrasion resistance, high corrosion resistance | Being widely used in standard die-part industry |
Copper Alloys No. | Materials | Temper | Dimensions (mm) | Main Properties | ||
Thicknesses | Widths | Length | ||||
C27200(Cu62) C26800(Cu65) C26200(Cu68) C26000(Cu70) C23000(Cu85) | Brass Plates with hot rolled | Hot Rolled | 4~8 | 600~2000 | 4000 max. | When thickness is 4~14mm, For C27200(Cu62) Rm (min.):290Mpa, A11.3(min.)30%. For C26200(Cu68),Rm (min.):290Mpa, A11.3(min.): 40%. |
8~60 | 600~3000 | 6000 max. | ||||
60~120 | 600~2000 | 4000 max. | ||||
C27200(Cu62) C26800(Cu65) C26200(Cu68) C26000(Cu70) C23000(Cu85) C22000(Cu90) | Brass Sheets and Plates with cold rolled | Soft, Hard | 0.5~3.0 | 1000 max. | 2500 max. | |
3.0~10 | 3000 max. | 6000 max. | ||||
Soft, H/2, Hard | 0.5~3.0 | 1000 max. | 2500 max. | |||
3.0~10 | 3000 max. | 6000 max. | ||||
Soft, H/4, H/2, Hard, Extra Hard. | 0.5~3.0 | 1000 max. | 2500 max. | |||
3.0~10 | 3000 max. | 6000 max. | ||||
Soft, H/2, Hard, Extra Hard | 0.5~3.0 | 1000 max. | 2500 max. | |||
3.0~10 | 3000 max. | 6000 max. | ||||
C37000 (HPb59-1) | Free Cutting Muntz metal | Hot Rolled | 4.0~8.0 | 550 max. | 3000 max. | When Thickness is 4 to 14mm, Rm(min.):370Mpa, A11.3(min.):18%. |
8.0~60 | 600 max. | 6000 max. | ||||
60~80 | 630 max. | 4000 max. | ||||
C37000 (HPb59-1) | Soft H/2 Hard. | 3.0~10 | 550 max. | 400 max. | ||
C46400 (HSn62-1) | Naval Brass | Hot Rolled | 4.0~8 | 600~2000 | 4000 max. | When Thickness is 4 to 14mm, Rm (Min.): 340Mpa A11.3(min.):20% |
8~60 | 600~3000 | 6000 max. | ||||
Hard H/2 Soft | 0.5~3.0 | 550 max. | 2000 max. | |||
3.0~10 | 2500 max. | 4000 max. | ||||
| GB | DIN | EN | ISO | UNS | JIS | ||
| H96 | CuZn5 | 2.022 | CuZn5 | CW500L | CuZn5 | C21000 | C2100 |
| H90 | CuZn10 | 2.023 | CuZn10 | CW501L | CuZn10 | C22000 | C2200 |
| H85 | CuZn15 | 2.024 | CuZn15 | CW502L | CuZn15 | C23000 | C2300 |
| H80 | CuZn20 | 2.025 | CuZn20 | CW503L | CuZn20 | C24000 | C2400 |
| H70 | CuZn30 | 2.0265 | CuZn30 | CW505L | CuZn30 | C26000 | C2600 |
| H68 | CuZn33 | 2.028 | CuZn33 | CW506L | CuZn35 | C26800 | C2680 |
| H65 | CuZn36 | 2.0335 | CuZn36 | CW507L | CuZn35 | C27000 | C2700 |
| H63 | CuZn37 | 2.0321 | CuZn37 | CW508L | CuZn37 | C27200 | C2720 |
| H62 | CuZn40 | 2.036 | CuZn40 | CW509N | CuZn40 | C28000 | C3712 |
| H60 | CuZn38Pb1.5 | 2.0371 | CuZn38Pb2 | CW608N | CuZn37Pb2 | C35000 | - |
| HPb59-1 | CuZn39Pb2 | 2.038 | CuZn39Pb2 | CW612N | CuZn38Pb2 | C37700 | C3771 |
| Temper | Temper | Tensile Rm MPa | Elongation A11.3(%)≥ | Hardness HV |
Soft | M | ≥290 | ≥40 | ≤90 |
| 1/4 hard | Y4 | 325-410 | ≥35 | 85-115 |
| 1/2 hard | Y2 | 355-460 | ≥25 | 100-130 |
| Hard | Y | 410-540 | ≥13 | 120-160 |
| Extra hard | T | 520-620 | ≥4 | 150-190 |
| Superhard | TY | ≥570 | ≥180 |
Name | Alloy No | Chemical Composition(%,Max.) | ||||||||
Cu | Fe | Pb | Al | Mn | Sn | Ni | Zn | Impurity | ||
Brass | H96 | 95.0-97.0 | 0.10 | 0.03 | --- | --- | --- | 0.5 | Rem | 0.3 |
H90 | 88.0-91.0 | 0.10 | 0.03 | --- | --- | --- | 0.5 | Rem | 0.3 | |
H85 | 84.0-86.0 | 0.10 | 0.03 | --- | --- | --- | 0.5 | Rem | 0.3 | |
H70 | 68.5-71.5 | 0.10 | 0.03 | --- | --- | --- | 0.5 | Rem | 0.3 | |
H68 | 67.0-70.0 | 0.10 | 0.03 | --- | --- | --- | 0.5 | Rem | 0.3 | |
H65 | 63.5-68.0 | 0.10 | 0.03 | --- | --- | --- | 0.5 | Rem | 0.3 | |
H63 | 62.0-65.0 | 0.15 | 0.08 | --- | --- | --- | 0.5 | Rem | 0.5 | |
H62 | 60.5-63.5 | 0.15 | 0.08 | --- | --- | --- | 0.5 | Rem | 0.5 | |
Trade terms: | FOB,CIF,CFR,EXW |
| Payment terms: | 1.L/C at sight 2.L/C 60/90 days 3.T/T 30% deposit and balance paid after goods are produced and before on board. 4.T/T 30% deposit and balance paid upon receipt of B/L copy 5.T/T 30% deposit and balance paid by L/C at sight. 6.T/T 30% deposit and balance paid by L/C 60/90 days |
| MOQ | 1ton |
| FOB price | USD450-1000/Ton FOB Tianjin |
| Sample time | 5 days |
| Lead time: | 15-35 days |
| Shipment: | by sea |
| Supply capability: | 5000 Tons |
| Sample availability | Yes |
| Packing Information: | plastic film inside and woven bag or hession cloth outside.25kg/50kg each coil,25ton/20'FCL(alsoaccording customer's requirment ). |