Pmdi Pm200 PU Raw Material Supply

China Pmdi Pm200 PU Raw Material Supply, Find details about China Mdi, Polymeric Mdi from Pmdi Pm200 PU Raw Material Supply

Appearance
Brown Liquid
Viscosity
150-250
Nco, %
30.5-32.0
Density
1.220-1.250
Acidity
0.05
Hydrolysable Chlorine
0.2
Trademark
Wanhua
Transport Package
Drums
Specification
220kg/drum
Origin
China
HS Code
3907209000
Appearance
Brown Liquid
Viscosity
150-250
Nco, %
30.5-32.0
Density
1.220-1.250
Acidity
0.05
Hydrolysable Chlorine
0.2
Trademark
Wanhua
Transport Package
Drums
Specification
220kg/drum
Origin
China
HS Code
3907209000
POLYMERIC PM200
Application
WANNATE PM-200 is a diisocyanate-diphenylmethane(MDI)-based composition containing some higher functionality isocyanates. The functionality is about 2.6-2.7. It is abrown liquid at ambient temperatures.
WANNATE PM-200 can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam,cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, WANNATE PM-200 can provide better flowability. It is, therefore, particularly suitable for the production which require strict flowability of systems.
Typical Physical and Chemical Properties
Test Item(s)Specification(s)
AppearanceBrown Liquid
Viscosity at 25ºC, mPa.S150-250
NCO, %30.5-32.0
Density 25ºC, g/cm31.220-1.250
Acidity (HCl), %≤0.05
Hydrolysable Chlorine, %≤0.2
Package(s)  210L iron drums, 250kg/drum
Storage
Since WANNATE PM-200 is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product.Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen.
Containers of WANNATE PM-200 should be kept properly closed and stored indoors at ambient temperature (15-35ºC) in a well-ventilated area. Storage at low temperature (below5ºC) may lead to some crystallization; this material must, therefore, be protected from frost.If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80ºC to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended.
Extended storage at temperatures above 50ºC is not recommended to prevent from the formation of insoluble solids and viscosity increase.
Shelf Life
Under recommended storage conditions, the shelf life of WANNATE PM-200 is one year since the date of production.

The above information is for reference only. The specific value still provided by  the manufacturer. Our company is not responsible for any legal liability.

 