Insulation Modified Polyolefin Fabric Heat Shrink Tubing

Products

Insulation Modified Polyolefin Fabric Heat Shrink Tubing

China Insulation Modified Polyolefin Fabric Heat Shrink Tubing, Find details about China Abrasion Resistant Fabric Tubing, Wear-Resisting Shrink Tubing from Insulation Modified Polyolefin Fabric Heat Shrink Tubing

Basic Info.

Model NO.

CL-KSD

Specification

6-100mm

Origin

Changzhou

Model NO.

CL-KSD

Specification

6-100mm

Origin

Changzhou

Product Desciption

Material(s) Description
Warp material: Polyester
Weft material: Irradiated, modified polyolefin
Coating: Modified polyolefin
Operating temperature range (3000 hours): -40°C to 125°C
Operating temperature range (1000 hours): -40°C to 150°C
Minimum recovery temperature: 110°C
Recommended recovery temperature :150°C to 200°C
Maximum storage temperature: 50°C
Standard:TL52668 TL52361 D44 1959 GMW14327
Testing organization:CTI PONY

Product description (CL-KSD)	Inside diameter (mm)
Product description (CL-KSD)	D (min.) expanded as supplied	d (max.) recovered after heating
φ6/3-B	6	3
φ8/4-B	8	4
φ10/5-B	10	5
φ12/6-B	12	6
φ16/8-B	16	8
φ20/10-B	20	10
φ25/12-B	25	12
φ30/15-B	30	15
φ35/17.5-B	35	17.5
φ40/20-B	40	20
φ50/25-B	50	25
φ60/30-B	60	30
φ70/35-B	70	35
φ80/40-B	80	40
φ100/50-B	100	50
B:black
Other specifications can be customized
Other specifications can be customized

Property	Test condition(s)	Performance
Thermal ageing	168 hrs at 125°C	No deterioration in abrasion resistance at 23°C
Thermal ageing	24 hrs at 125°C	No deterioration in abrasion resistance at 23°C
Flammability	MVSS 302	Burning rate≤100 mm/min
Low temperature flexibility	4 hours at -40°C,10X diameter mandrel	No cracking
Abrasion resistance (1.5N load, 0.3mm radius metal blade,60 cpm,50mm stroke, 144 000 cycles)	Environmental Chamber Temperature: -35°C	No wear to underlying rubber hose
	Environmental Chamber Temperature: 140ºC	No wear to underlying rubber hose
Temperature resistance 1) Test temperature 140 ºC, for 500 hours 2) Remove the sample and cool it to room temperature..Then place the sample at -35°C for 22 hours. 3) Then bend the sample 180 degrees around a cylinder with a radius of 30mm	Test temperature 140 ºC, for 500 hours	The protection tube is not damaged Standard: TL52668