Feature
Anti-uv
Shrinking temperature: Start at 70° C, shrunk totally at 125° C
Operating temperature: -45° C~110° C
Shrink Ratio: 3:1, 4:1
Color: Black( any colors can be request)
Medium wall heat shrink tube, Adhesive heat shrink tube, heat shrikable sleeve
Description
Medium&heavy wall heat shrink tube is manufactured by polyolefin and hot melt adhesive. Used for insulating and protecting middle connections and terminals of medium& low voltage cable, busbars and other places where flame retardance is demanded and resisting corrosion and abrasion for pipelines.
| Property | Test Result | Test Method |
| Tensile strength | ≥14Mpa | ASTM D 2671 |
| Elongation | ≥400% | ASTM D 2671 |
| Tensile strength after aging | ≥12Mpa | 158 °C x 168h |
| Elongation after aging | ≥300% | 158 °C x 168h |
| Longitudinal change | -8%~+8% | ASTM D 2671 |
| Dielectric strength | ≥20kv/mm | IEC 60243 |
| Volume resistivity | ≥1014Ω.cm | IEC 60243 |
| Water-absorption | 0.50% | ASTM D 570 |
| Thermal shock | no cracking no dripping | 225 °C x 4h |
| Property | Test Result | Test Method |
| Softening point | 95 °C ±5 °C | ASTM E28 |
| Water-absorption | 0.005 | ASTM D 570 |
| Peel strength(PE) | ≥120N/25mm | ASTM D 1000 |
| Peel strength(AL) | ≥80N/25mm | ASTM D 1000 |
| Size (mm) | As Supplied (mm) | M/pcs |
| Φ6.0 /2.0 | ≥6.0 | 1.22 |
| Φ8.0 12.0 | ≥8.0 | 1.22 |
| Φ10.2 / 3.0 | ≥10.2 | 1.22 |
| Φ12.0 / 3.0 | ≥12.0 | 1.22 |
| Φ16.0 / 5.0 | ≥16.0 | 1.22 |
| Φ19.1 / 5.6 | ≥19.1 | 1.22 |
| Φ22.0 / 6.0 | ≥22.0 | 1.22 |
| Φ25.0 / 8.0 | ≥25.0 | 1.22 |
| Φ28.0 / 6.0 | ≥28.0 | 1.22 |
| Φ33.0 / 8.0 | ≥33.0 | 1.22 |
| Φ38.1 / 12.0 | ≥38.1 | 1.22 |
| Φ43.2 / 12.7 | ≥43.2 | 1.22 |
| Φ55.0 / 16.0 | ≥55.0 | 1.22 |
| Φ65.0 / 19.0 | ≥65.0 | 1.22 |
| Φ75.0 / 22.0 | ≥75.0 | 1.22 |
| Φ85.0 / 25.0 | ≥85.0 | 1.22 |
| Φ95.0 / 30.0 | ≥95.0 | 1.22 |
| Φ115 / 34.0 | ≥115 | 1.22 |
| Φ140 / 42.0 | ≥140 | 1.22 |
| Φ160 / 50.0 | ≥160 | 1 |
| Φ180 / 65.0 | ≥180 | 1 |
| Φ200 / 69.0 | ≥200 | 1 |
| Φ230 / 78.0 | ≥230 | 1 |