Description:
Dyneon Fluoroelastomer FE 5540 is a terpolymer made of vinylidene fluoride, hexafluoropropylene, and tetrafluoroethylene containing 65.5% fluorine. This fluoroelastomer is ideal for automotive fuel system and oil seal applications. Its proprietary incorporated bisphenol cure technology may help save time and increase throughput. 
Dyneon FE 5540 has a number of favorable attributes that make it suitable for use in compression and transfer molding. It boasts improved low-temperature flexibility over standard copolymers and terpolymers,and delivers good compression set resistance.Additionally,the proprietary incorporated cure technology may help save time and increase throughput.
Dyneon FE 5540 can be compounded using standard water-cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formulations. The dry ingredients should be blended before adding to the masticated gum. For best results, Dyneon fluoroelastomer FE 5540 should be banded on the mill prior to adding the blended dry ingredients. Once mixed, the compounded stocks have good scorch resistance and storage stability.

Dyneon Fluoroelastomer FE 5610 is a low viscosity copolymer of vinylidene fluoride and hexafluoropropylene with 66% fluorine. This fluoroelastomer (FKM) has proprietary incorporated cure technology that may help save time and increase throughput.
Dyneon FE 5610 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formulations. The dry ingredients should be blended before adding to the masticated gum. For best results, Dyneon FE 5610 should be banded on the mill several minutes prior to adding the blended dry ingredients. Once mixed, the compounded stocks have good scorch resistance and storage stability.
FE 5610 has a number of excellent attributes that make it well-suited for use in high temperatures, injection molding and transfer molding applications. First, this product has improved mold release properties and better cure response to higher molding temperatures. Additionally, FE 5610 can be utilized as a viscosity modifier, and contains a proprietary incorporated cure technology that may help save time and increase throughput.

Dyneon Fluoroelastomer FE 5620Q is a copolymer of vinylidene fluoride and hexafluoropropylene with a fluorine content of 65.9%. This fluoroelastomer (FKM) is the low-viscosity version of Dyneon Fluoroelastomer FE 5640Q used in transfer and injection molding, extrusion and calendering. It offers improved scorch resistance at high molding temperatures.Dyneon Fluoroelastomer FE 5620Q offers excellent mold release, meaning it can be used in automated injection molding equipment. Additionally, it features an improved proprietary incorporated cure technology that results in a more consistent part size from successive molding cycles.
Dyneon fluoroelastomer FE 5620Q can be compounded using standard water-cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical FKM formulations. The dry ingredients should be blended before adding to the masticated gum. For best results, FE 5620Q should be banded on the mill prior to adding the blended dry ingredients. Once mixed, the compounded stocks display excellent processing characteristics and storage stability.

Dyneon FE 5621 is a copolymer of vinylidene fluoride and hexafluoropropylene with a fluorine content of 65.9%. This fluoroelastomer (FKM) is the low-shrinkage version of Dyneon FE 5620Q, and can be used in transfer and injection molding, extrusion and calendering. It offers improved scorch resistance at high molding temperatures.
Dyneon FE 5621 offers excellent mold release, meaning it can be used in automated injection molding equipment. Additionally, it features an improved proprietary incorporated cure technology that results in a more consistent part size from successive molding cycles.
Dyneon fluoroelastomer FE 5621 can be compounded using standard water-cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical FKM formulations. The dry ingredients should be blended before adding to the masticated gum. For best results, FE 5621 should be banded on the mill prior to adding the blended dry ingredients. Once mixed, the compounded stocks have good scorch resistance and storage stability.

Dyneon FE 5622Q is a copolymer of vinylidene fluoride and hexafluoropropylene with a 65.9% fluorine content. This fluoroelastomer (FKM) is targeted for bonded shaft seal applications. It offers improved scorch resistance at high molding temperatures, and its proprietary incorporated curative may help save you time and increase throughput.
Dyneon Fluoroelastomer FE 5622Q can be used in automated injection molding equipment, because it exhibits excellent mold release. It also features properties that make it ideal for demanding bonded shaft seal applications.
Dyneon fluoroelastomer FE 5622Q can be compounded using standard water-cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical FKM formulations. The dry ingredients should be blended before adding to the masticated gum. For best results, FE 5622Q should be banded on the mill prior to adding the blended dry ingredients. Once mixed, the compounded stocks have good scorch resistance and storage stability.