Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet

China Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet, Find details about China Lanthanum Molybdenum Charge Carrier, Mlr Sheet from Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet

Model NO.
SHIBO-MLR sheet
Density
10.2g/cm3
Surface
Cold Rolled, Hot Rolled, Alkali, Annealing
Thickness
0.1mm to 200mm
Width
20mm to 800mm
Length
3000mm Max
Trademark
Shibo
Transport Package
Wooden Case with Foam Board
Specification
ISO9001
Origin
China
HS Code
81029500
Model NO.
SHIBO-MLR sheet
Density
10.2g/cm3
Surface
Cold Rolled, Hot Rolled, Alkali, Annealing
Thickness
0.1mm to 200mm
Width
20mm to 800mm
Length
3000mm Max
Trademark
Shibo
Transport Package
Wooden Case with Foam Board
Specification
ISO9001
Origin
China
HS Code
81029500
Charge carrier Base-plate made from LANTHANUM oxide Doped Molybdenum Material, MLR sheet 

Mo has a unique property of which it's melting point can reach 2610C, it is widely applied in high temperature vacuum furnace melting environment such as sapphire growing furnace, quartz glass melting furnace, and rare earth melting furnace. The working temperature of  Mo sheet is above 1500.
 
Physical and chemical properties
(1) Density: 10.2g/cm3
(2) Surface roughness: < 1.6
(3) Purity: La 0.4-0.6%, Mo the balance
(4) Application temperature environment:1500~1800
 
Specifications:
Thickness: 0.1mm to 200mm
Width: 10mm to 800mm
Length: 3000mm max
 Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet
Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet
Specifications:
Molybdenum sheets/plates
Thickness(mm)tolerances(mm)width(mm)tolerances(mm)length(mm)tolerances(mm)flatness(%)
0.1mm±0.01600mm±1mm2000mm±5mm< 2%
0.2mm±0.02600mm±1mm2000mm±5mm< 2%
0.3mm±0.02600mm±1mm2000mm±5mm< 2%
0.4mm±0.03600mm±1mm2000mm±5mm< 2%
0.5mm±0.03600mm±1mm2000mm±5mm< 2%
0.8mm±0.05600mm±1mm2000mm±5mm< 2%
1mm±0.06600mm±1mm2000mm±5mm< 2%
1.5mm±0.06600mm±1mm2000mm±5mm< 2%
2mm±0.06600mm±1mm2000mm±5mm< 2%
3mm±0.2500±1mm500±2mm< 2%
4mm±0.2500±1mm500±2mm< 2%
 
 
Test analysis:
ElementW/%ElementW/%
Pb<0.0001Al<0.0001
Bi<0.0001Si<0.001
Sn<0.0001Ca<0.001
Sb<0.0001Mg<0.001
Cd<0.001P0.0002
Fe0.0050C0.0016
Ni0.0007N0.0020
O0.0050Mo99.98
 
Usage: used for processing molybdenum disks, and foils. They are used as heat shields in high-temperature vacuum and hydrogen-atmosphere furnace construction
Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet

Photos of our factory
Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet

Charge Carrier Base-Plate Made From Lanthanum Oxide Doped Molybdenum Material, Mlr Sheet