China Diesel Resistant Heat Shrinkable Tubing, Find details about China 150 Degrees Heat Shrink Tube, High Temperature Resistant Tube from Diesel Resistant Heat Shrinkable Tubing
| Item | CL-DR |
| Continuus Temperature Range | -55ºC~150ºC |
| Radial Shrinking Ratio | 2:1 |
| Longitudinal Shrinking Ratio | ±10% |
| Dielectric Voltage Withstand | 600V |
| Environmental standards | ROHS REACH |
| Color | Black |
| Flammability | VW-1 |
| Performance Testing | Test Methods | Performance indicators | ||
| Tensile Strength(MPa) | ASTM D2671 | ≥13.8 | ||
| Elongation Ratio(%) | ASTM D2671 | ≥300% | ||
| Tensile Strength(MPa) | ASTM D2671(150ºC/168h) | ≥10.3 | ||
| Elongation Ratio(%) | ASTM D2671 (150ºC/168h) | ≥300% | ||
| Fluid resistance | 0#Diesel | Tensile Strength(MPa) | ASTM D2671 (23ºC/24h) | ≥10.3 |
| Elongation Ratio(%) | ≥300% | |||
| Weight gain ratio | <=15% | |||
| IRM902 | Tensile Strength(MPa) | UL-224 70ºC/4h , | Retention rate≥75% | |
| Elongation Ratio(%) | Retention rate≥75% | |||
| Weight gain ratio | <=15% | |||
| IRM903 | Tensile Strength(MPa) | ASTM D2671 (70ºC/ 24h) | ≥10.3 | |
| Elongation Ratio(%) | ≥300% | |||
| Weight gain ratio | <=20% | |||
| Copper corrosion | Copper corrosion | ASTM D2671(150°C/168) | No brittleness, glass tube or crack; no pitting copper | |
| Elongation Ratio(%) | ≥200% | |||
| Size | supplied(mm) | After heating(mm) | Package | |
| min ID (Inside Diameter) | Max ID (Inside Diameter) | T(Wall-thickness) | (Meter/Roll) | |
| Φ3.2 /1.6 | 3.2 | 1.6 | 0.76±0.15 | 100 |
| Φ4.8/2.4 | 4.8 | 2.4 | 0.85±0.15 | 100 |
| Φ6.4/3.2 | 6.4 | 3.2 | 0.89±0.15 | 100 |
| Φ9.5/4.8 | 9.5 | 4.8 | 1.02±0.20 | 50 |
| Φ12.7/6.4 | 12.7 | 6.4 | 1.22±0.20 | 50 |
| Φ19.1/9.5 | 19.1 | 9.5 | 1.45±0.28 | 50 |
| Φ25.4/12.7 | 25.4 | 12.7 | 1.78±0.28 | 25 |
| Φ38.1/19.0 | 38.1 | 19 | 2.41±0.41 | 25 |
| Φ50.8/25.4 | 50.8 | 25.4 | 2.79±0.41 | 20 |
| Remarks: Special specifications, sizes and special packaging requirements can be customized according to customer requirements. | ||||