China Abrasion Wear Ar500 Mn13 Nm500 Wear Resistant Steel Plate, Find details about China Wear Resistant Steel Plate, Abrasion Steel Plate from Abrasion Wear Ar500 Mn13 Nm500 Wear Resistant Steel Plate
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.11-0.20 | 0.38-0.55 | 1.20-1.55 | 0.005-0.020 | 0.005-0.010 | 0.01-0.60 | 0.004-0.04 | |
Hardness | 370-430HB | |||||||
Michanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tebsile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1050 | >1250 | 12 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 40 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.20-0.26 | 0.75-0.95 | 1.60-1.80 | 0.015-0.020 | 0.005-0.010 | 0.01-0.60 | 0.001-0.04 | |
Hardness | 420-480HB | |||||||
Michanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tebsile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1150 | >1300 | 10 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 30 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.25-0.35 | 0.25-1.75 | 0.40-1.60 | 0.015-0.020 | 0.005-0.010 | 0.20-0.80 | 0.001-0.03 | |
Hardness | 470-530HB | |||||||
Michanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tebsile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1250 | >1500 | 8 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 20 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.30-0.37 | 0.2-0.405 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.30-0.80 | 0.002-0.60 | |
Hardness | 520-580HB | |||||||
Michanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tebsile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1300 | >1550 | 6 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 12 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.35-0.40 | 0.20-0.80 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.25-1.00 | 0.002-0.60 | |
Hardness | 560-620HB | |||||||
Michanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tebsile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1450 | >1650 | 5 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 8 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.40-0.50 | 0.20-0.80 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.80-1.50 | 0.002-0.60 | |
Hardness | 620-680HB | |||||||
Michanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tebsile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1500 | >1750 | 3 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 6 |