Lead-Acid Battery Separator Glass Fiber Mat

China Lead-Acid Battery Separator Glass Fiber Mat, Find details about China Battery Separator Fiberglass Tissue, Glass Fiber Battery Separator Surfacing Mat from Lead-Acid Battery Separator Glass Fiber Mat

Model NO.
XGBS0.6
Width
1000mm
Moisture
<0.2%
Binder Content
<20%
Tensile Strength
>120n/50mm
Fiber Diameter
13um
Roll Length
2000m
Thickness
0.6mm
Acid Resistance/15minutes
≤2%
Trademark
XIANGU
Transport Package
164.00kg Per Roll
Specification
1170*1170*1060mm
Origin
Shenzhen
HS Code
7019310000
Model NO.
XGBS0.6
Width
1000mm
Moisture
<0.2%
Binder Content
<20%
Tensile Strength
>120n/50mm
Fiber Diameter
13um
Roll Length
2000m
Thickness
0.6mm
Acid Resistance/15minutes
≤2%
Trademark
XIANGU
Transport Package
164.00kg Per Roll
Specification
1170*1170*1060mm
Origin
Shenzhen
HS Code
7019310000
lead-acid battery separator glass fiber mat/Battery separator mat is mainly used as lead-acid battery separator,it has a smooth surface,uniform thickness, low DC resistance,high liquid absorption,good acid-proof property,low content of reducing agent potassium permanganate and impurity,good stiffness.The substrate for lead-acid battery separator plate made of this mat has good mechanic strength and vibration resistance, low mass resistivity, high porosity and large capacity. Battery installed with this series mat has strong starting ability and long lifespan.So that it is widely used in the battery field and it has become the main substrate material for battery separator plate.

SPECIFICATIONS:
Model:XGBS0.6
Thickness(mm):0.6±0.04
Thickness deviation(%):≤5
Binder Content(%):<20
Tensile Strength MD(N/50mm):≥120
Acid resistance/15minutes(%):≤2
Acid resistance/72hrs(%):<3
Wetting time(s):≤10
Reduce KMnO4 Material /(1/5 KMnO4)=0.01mol/L(g /ml):≤15
Cl content(%):≤0.003
Fe content(%):≤0.005
Width(mm):1000±5/customized
Roll Length(m):2000
Roll Diameter(mm):1170
Paper tube Internal Diameter(mm):152
 
STORAGE:
The mat should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.

PACKAGING:
Lead-Acid Battery Separator Glass Fiber Mat
 
SHIPMENT AND TRANSPORTATION:
Shipment by sea:for sea transportation,generally 40HQ container can load 44rolls ,total 88000.00m2,net weight 5068.80kg.
 
OEM INFORMATION:
Other mat can be produced by customer's specifications.
ITEMUNITMODEL
XGBS0.3XGBS0.4XGBS0.5XGBS0.6XGBS0.8
Thicknessmm0.3±0.030.4±0.030.5±0.040.6±0.040.8±0.05
Binder Content%<20
Tensile Strength MDN/50mm≥60≥80≥100≥120≥160
Acid resistance/15hours%≤2
Acid resistance/72hours%<3
Thickness deviation%≤5
Wetting timeS≤100≤25≤10≤10≤10
Reduce KMnO4 Material (1/5 KMnO4)=0.01mol/Lg /ml≤15
Cl content%≤0.003
Fe content%≤0.005
Widthmm1000±5/customized
Roll Lengthm25002500200020001500
Roll Diametermm<1170
Paper Tube Internal Dia.mm76 152
 