3mm Kevlar Chopped Strands

China 3mm Kevlar Chopped Strands, Find details and Price about China 3mm Kevlar Chopped Strands, PARA-Aramid Chopped Strands from 3mm Kevlar Chopped Strands

Basic Info.

Model NO.

XGPF1203

Width

1.5D

Function

High Strength Fiber

Structure

Miscellaneous Chain Synthetic

Model

Xgpf1203

Colors

Yellowish

Fiber

PARA-Aramid

Density

1.47g/cm3

P-Aramid Content

100%

Average Fiber Length

3mm

Tensile Strength

19.4-21 Cn/Dtex

Tensile Modulus

80gpa~120gpa

Elongation at Break

2.5%-3.84%

Moisture

<0.2%

Trademark

XIANGU

Transport Package

5kg Per Bag

Specification

ROHS

Origin

Guangdong

HS Code

54021190

Model NO.

XGPF1203

Width

1.5D

Function

High Strength Fiber

Structure

Miscellaneous Chain Synthetic

Model

Xgpf1203

Colors

Yellowish

Fiber

PARA-Aramid

Density

1.47g/cm3

P-Aramid Content

100%

Average Fiber Length

3mm

Tensile Strength

19.4-21 Cn/Dtex

Tensile Modulus

80gpa~120gpa

Elongation at Break

2.5%-3.84%

Moisture

<0.2%

Trademark

XIANGU

Transport Package

5kg Per Bag

Specification

ROHS

Origin

Guangdong

HS Code

54021190

Product Desciption

3mm kevlar chopped strands was chopped in 3mm by a special cutting equipment. This fiber has high strength and modulus, strong hydrogen bonding strength, strength up to 28 g/d or more, strength is 5-6 times of steel wire.specific modulus 2-3 times of it,toughness 2 times of it while weight is just 1/5 of the wire.Continuous using temperature range is extremely wide, long running in the range of -196 ºC to 204 ºC,no decomposition and melting at high temperature of 560 ºC,strength can maintain 75% through 100 hours at 200 ºC.also has good chemical solvent resistance, resisting acid and alkali, anti-aging, good adhesion to rubber. Usually it is used as a reinforcing material in the fields of thermoplastics, thermosetting plastics, high-temperature composite structures, brake pads, clutch linings, friction material, wear-resistant filler, cable sheathing, gaskets, slot insulation, phase insulation barrier, interturn insulation and so on.

SPECIFICATIONS:

Model:	XGPF1203
Color:	yellowish
Fiber type:	Para-aramid
Density(g/cc)	1.47
Linear density of mono filament(D)	1.5
Filament diameter(μm)	12
Fiber length(mm)	3
Tensile strength( cN/dtex)	19.4-21
Elongation at break(%)	2.5-3.84
Tensile modulus(GPa)	80~120
Shrinkage(%)	<0.2(190ºC×15m)
Moisture (%):	<0.2

APPLICATION FIELDS:

1.Engineering Plastics,thermosetting resin,friction materials, automotive brakes,composite materials and Kevlar reinforced paper.

2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.

3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.

4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.

STORAGE:

The 3mm kevlar chopped strands should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire