China Waterproof Polyolefin Single Wall Heat Shrink Tube with UL, Find details about China Heat Shrink Tube, Heat Shrinkable Tubing from Waterproof Polyolefin Single Wall Heat Shrink Tube with UL
SPECIFICATIONS | |
MATERIAL: | POLYOLEFIN (CROSSLINKED) |
FEATURE: | FLAME RETARDANT |
VOLTAGE: | 600 V |
STANDARD: | UL 224 125°C & RoHS |
WALL TYPE: | SINGLE |
SHRINK TEMP: | 90°C |
WORK TEMP: | -55°C~125°C |
RATIO: | 2:1 |
UL FILE: | E197895 |
EASE CODE | ||||||
AS SUPPLIED (mm) | AFTER RECOVERY (mm) | |||||
Inside Diameter (D) | Wall Thickness (T) | Inside Diameter (D) | Wall Thickness (T) | |||
(D) | (T) | (d) | (t) | |||
mm | inch | mm | mm | inch | mm | |
HS-SW-1.2/0.6-LT | ≥1.2 | 3/64 | 0.20 ± 0.08 | ≤0.6 | 3/128 | 0.40 ± 0.08 |
HS-SW-1.6/0.8-LT | ≥1.6 | 1/16 | 0.20 ± 0.08 | ≤0.8 | 1/32 | 0.40 ± 0.08 |
HS-SW-2.4/1.2 | ≥2.4 | 3/32 | 0.20 ± 0.09 | ≤1.0 | 3/64 | 0.42 ± 0.08 |
HS-SW-3.2/1.6 | ≥3.2 | 1/8 | 0.25 ± 0.09 | ≤1.5 | 1/16 | 0.48 ± 0.10 |
HS-SW-4.8/2.4 | ≥4.8 | 3/16 | 0.25 ± 0.09 | ≤2.0 | 3/32 | 0.54 ± 0.10 |
HS-SW-6.4/3.2 | ≥6.4 | 1/4 | 0.28 ± 0.10 | ≤3.0 | 1/8 | 0.50 ± 0.10 |
HS-SW-9.5/4.7 | ≥9.5 | 3/8 | 0.30 ± 0.12 | ≤4.5 | 3/16 | 0.72 ± 0.12 |
HS-SW-12.7/6.3 | ≥12.7 | 1/2 | 0.30 ± 0.12 | ≤6.0 | 1/4 | 0.72 ± 0.12 |
HS-SW-16/8 | ≥16.0 | 5/8 | 0.36 ± 0.12 | ≤8.0 | 5/16 | 0.70 ± 0.12 |
HS-SW-19.1/9.5 | ≥19.1 | 3/4 | 0.38 ± 0.15 | ≤10.0 | 3/8 | 0.80 ± 0.15 |
HS-SW-25.4/12.7 | ≥25.4 | 1 | 0.42 ± 0.15 | ≤12.5 | 1/2 | 0.90 ± 0.15 |
HS-SW-32/16 | ≥32.0 | 1-1/4 | 0.45 ± 0.15 | ≤15.0 | 5/8 | 0.97 ± 0.15 |
HS-SW-38.1/19 | ≥38.1 | 1- 1/2 | 0.50 ± 0.15 | ≤21.0 | 3/4 | 1.10 ± 0.15 |
HS-SW-50.8/25.4 | ≥50.8 | 2 | 0.50 ± 0.15 | ≤27.0 | 1 | 1.10 ± 0.15 |
HS-SW-76.2/38.1 | ≥76.2 | 3 | 0.70 ± 0.30 | ≤38.1 | 1-1/2 | 1.25 ± 0.20 |
HS-SW-101.6/50.8 | ≥101.6 | 4 | 0.70 ± 0.30 | ≤50.8 | 2 | 1.25 ± 0.20 |
HS-SW-127/63.5 | ≥127.0 | 5 | 0.70 ± 0.30 | ≤63.5 | 2-1/2 | 1.40 |
HS-SW-152.4/76.2 | ≥152.4 | 6 | 0.70 ± 0.30 | ≤76.2 | 3 | 1.40 |
HS-SW-177.8/88.9 | ≥177.8 | 7 | 0.70 ± 0.30 | ≤88.9 | 3-1/2 | 1.40 |
HS-SW-203.2/101.6 | ≥203.2 | 8 | 0.70 ± 0.30 | ≤101.6 | 4 | 1.40 |
HS-SW-228.6/114.3 | ≥228.6 | 9 | 0.70 ± 0.30 | ≤114.3 | 4-1/2 | 1.40 |
TECHNICAL DATA |
PROPERTY | DATA | CONDITION |
Tensile Strength | ≥10.4MPa | |
Tensile Strength After Aging | ≥7.3MPa | 158°C ± 1.0°C, 168 hrs |
Elongation | ≥200% | |
Elongation After Aging | ≥100% | 134°C 60 days |
Longitudinal Change | <±5% | |
Radial Shrinking Ratio | ≥50% | |
Flammability | VW-1 | |
Dielectric Strength | No Breakdown | At 1 Min, AC2500V |
Volume Resistivity | ≥10 * 1012 Ω.cm | |
Corrosion | No Corrosion | |
Copper Stability | ≥100% | |
Concentricity | 70% |