RTV2 Electronic Potting Liquid Rubber Silicone for Encapsulation Coating

China RTV2 Electronic Potting Liquid Rubber Silicone for Encapsulation Coating, Find details about China Electronic Potting Compound, Silicone Rubber for Encapsulation from RTV2 Electronic Potting Liquid Rubber Silicone for Encapsulation Coating

Basic Info.

Model NO.

HY-9055

Operate Time

1-2 Hours

Curing Time

6-8 Hours

Color

Grey/Black/Transparent or Others

MOQ

200kgs

Trademark

Hong Ye Silicone Rubber

Transport Package

25kg/Drum 200kg/Drum

Specification

RoHS, ISO-2001, SGS

Origin

China

HS Code

39100000

Model NO.

HY-9055

Operate Time

1-2 Hours

Curing Time

6-8 Hours

Color

Grey/Black/Transparent or Others

MOQ

200kgs

Trademark

Hong Ye Silicone Rubber

Transport Package

25kg/Drum 200kg/Drum

Specification

RoHS, ISO-2001, SGS

Origin

China

HS Code

39100000

Product Desciption

HY-9055 Electronic Potting Compound
Description
HY-9055 is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time.

Application
HY-9055 is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB, substrate, etc.

Technical Parameters

Model

Color

Viscosity (cps)

Hardness (A°)

Mixing ratio

Operating
Time(min)

Curing
Time(hr, 25ºC)

Thermal conductivity
w(m.k)}

dielectric strength(kV/mm)

dielectric constant(1.2MHz)

Volume resistivity(Ω.cm)

coefficient of linear expansionm/(m.k)

flame retardation

HY-9025

Grag

500±500

25±5

1:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-9045

Grag

2500±500

45±5

1:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-9055

Grag

3000±500

55±5

1:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-9300

Water clear

1800±800

1:1

1~2

12~14

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-9305

Water clear

500±100

5±3

1:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-9310

Water clear

500±100

10±3

1:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-9320

Water clear

1000±100

20±3

1:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-9330

Water clear

500±100

30±3

1:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-210

Transparent

1800±800

15±3

10:1

30~60

4~5

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

HY-215

Black/ Light yellow/ Red brown

2500±800

15±3

10:1

60~120

6~12

≥0.2

≥25

3.0-3.3

≥1.0x10*16

≤2.2x10*-4

94-V0

(Pls note: the above data for this product in 25 ºC temperature, 55 percent humidity conditions, for reference. The accurate data is measured by customers when using.)

TECHNICAL GUIDELINES
1, Typical Application
HY-9055 could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
- It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. Pls put part A and part B in separate container and stir evenly before mixing the two part together.

2, Mixing Ratio: part A: part B = 1:1

3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.

4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100ºC, the silicone will cure in 15 minutes; while in 25ºC room temperature, the silicone will cure around 8 hours.

RTV2 Electronic Potting Liquid Rubber Silicone for Encapsulation Coating

RTV2 Electronic Potting Liquid Rubber Silicone for Encapsulation Coating

Notes:
1.The following material may hinder the curing of HY-9055, so pls use after the test. When necessary, pls clean the application areas.
Organotin compound or Condensation silicone with organotin
Sulphur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux
2. HY-9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.
3. HY-9055 belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance.

PACKAGE:
20Kg/pail as a set (Part A 10Kg + Part B 10Kg)
RTV2 Electronic Potting Liquid Rubber Silicone for Encapsulation Coating

SHELF LIFE AND TRANSPORTATION

Twelve(12) months when stored at 25C in tightly closed original packages.

This kind of product is non-dangerous product, which could be transported as general chemicals.

3. Storage beyond the expired date does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.
RTV2 Electronic Potting Liquid Rubber Silicone for Encapsulation Coating