4Cr13 /1.2083/420/ 4Cr13 Steel Flat for Injection Mould, Blowing Mould
China 4Cr13/1.2083/420/4Cr13 Steel Flat for Injection Mould, Blowing Mould, Find details about China 1.2083 Steel, Hot Runner Plastic Mold from 4Cr13/1.2083/420/4Cr13 Steel Flat for Injection Mould, Blowing Mould
GB 4Cr13 for making plastic mold and hot runner
Equivalence
| AlSl / SAE | DIN / W.Nr | JIS | GB | ||||||||
| 420 | 1.2083 | SUS420J2 | 4Cr13 | ||||||||
Chemical Composition (%)
| Steel Grade | C | Si | Mn | P | S | Cr | |||||||
| 1.2083 | 0.36 | ≤ | ≤ | ≤ | ≤ | 12.50 | |||||||
| 0.42 | 1.00 | 1.00 | 0.030 | 0.030 | 14.50 | ||||||||
| 420 | ≤ | ≤ | ≤ | ≤ | ≤ | 12.00 | |||||||
| 0.15 | 1.00 | 1.00 | 0.030 | 0.030 | 14.00 | ||||||||
| 4Cr13 | 0.36 | ≤ | ≤ | ≤ | ≤ | 12.00 | |||||||
| 0.45 | 0.60 | 0.80 | 0.030 | 0.030 | 14.00 |
Dimensions
| Shape | Thick / Dia.(mm) | Width(mm) | ||||||
| Flat | 6-200 | 20-910 | ||||||
| Plate | 6-120 | 1000-2300 | ||||||
| Block | 150-600 | 200-1500 |
Delivery Condition
EAF+LF+VD+(ESR), Forged, Unmachined or Machined surface, UT 100% Passed
We offer two conditions as
Annealed: Hardness≤235HB
Q+T: Hardness 33-38HRC or as customized
Characteristics
Martensite stainless steel, with good machincability and excellent corrosion resistance, polishability, and high strength and wear resistance after heat treatment.
Application
It is also widely used for making plastic moulds and transparent plastic molds which require high load, wear resistance, and work under the action of corroding medium.
Forging Technique
Heat Treatment
| Heat Temperature | Start Forging Temperature | Finish Forging Temperature | Cooling Method |
| Slowly heat to 800ºC,then quickly heat to final forging temperature | 1160-1200ºC | >=850ºC | Ash coolinor sand cooling,with timely annealing |
Annealing
840 to 870°C
Slow controlled cooling in furnace at a rate of 10 to 20°C/hr down to approx. 600°C, further cooling in air. Hardness after annealing: max. 229 HB.
Stress relieving
Approx. 650°C
Slow cooling in furnace; intended to relieve stresses set up by extensive machining, or in complex shapes. After through heating, hold in neutral atmosphere for 1 - 2 hours.
Hardening
1000 to 1050°C / Oil, air
Holding time after temperature equalization: 15 to 30 minutes.
Obtainable hardness: 53-56 HRC
Tempering
100 to 200°C (212 to 392°F)
Slow heating to tempering temperature immediately after hardening / time in furnace
1 hour for each 20 mm of work piece thickness but at least 2 hours / cooling in air.
For average hardness figures to be obtained please refer to the tempering chart.
What we can offer?
We offer a wide range of steel products in a wide variety of dimensions and executions, acc.to the common international specifications or customerized.
Machining and heat treatment are available.
Also, we advise you in choosing the right materials.
Shape Available
Solid round bar
Flat bar
Square bar
Hexagon bar
Block
Plate
Sheet
Wire rod
Strip
| AISI | DIN | JIS | Stock | Application |
Hot Work Tool Steel | H11 | 1.2343 | SKD6 | √ | Die Casting Dies,Extrusion Dies, Hammer Dies, |
H13 | 1.2344 | SKD61 | √ | ||
H10 | 1.2365 | SKD7 |
| ||
-- | 1.2367 | -- |
| ||
L6 | 1.2714 / 1.2713 | SKT4 | √ | ||
H12 | 1.2606 | SKD62 |
| ||
H21 | 1.2581 | SKD5 | √ | ||
Cold Work Tool Steel | D3 | 1.2080 | SKD1 | √ | Cutting Tools, Punching Tools, Shear Bladers, Reamers, Thread Rolling Dies, Calipers, Sockets etc. |
-- | 1.2601 | ~SKD11 | √ | ||
D2 | 1.2379 | ~SKD11 | √ | ||
-- | 1.2379 MOD | DC53 (Daido) | √ | ||
D6 | 1.2436 | -- |
| ||
O1 | 1.2510 | SKS3 | √ | ||
O2 | 1.2842 | -- |
| ||
A2 | 1.2363 | SKD12 |
| ||
S1 | 1.2550 | -- |
| ||
S7 | 1.2357 | -- |
| ||
-- | 1.2767 | SKT6 |
| ||
L2 | 1.2210 | -- |
| ||
Plastic | P20 | 1.2311 | -- | √ | Mold Base, Core & Cavity, Bumper Mold etc. |
P20+Ni | 1.2738 | -- | √ | ||
P20+S | 1.2312 | -- | √ | ||
-- | 1.2316 | -- |
| ||
420 | 1.2083 | SUS420J2 | √ | ||
-- | -- | NAK80 (Daido) | √ | ||
Alloy Steel | 4120 | 25CrMo4 / 1.7218 | SCM420 |
| Shafts, Gears, Drillers, Chains, Bolts, Nuts, Pins, Suds, Keys, Bites, Crankshafts, Connecting Rods, Came, Couplings etc. |
4135 | 34CrMo4 / 1.7220 | SCM435 |
| ||
4130 | 34CrMo4 / 1.7220 | SCM430 | √ | ||
4140 | 42CrMo4 / 42CrMoS4 / 1.7225 | SCM440 | √ | ||
4142 | 41CrMo4 / 1.7223 | SCM440 |
| ||
4145H | -- | -- |
| ||
4330V | -- | -- |
| ||
4340 | 34CrNiMo6 / 1.6582 | SNCM439 |
| ||
5115 | 16MnCr5 / 16MnCrS5 / 1.7131 |
|
| ||
5120 | 20MnCr5 / 20MnCrS5 / 1.7147 | SMnC420H |
| ||
5140 | 41Cr4 / 41CrS4 / 1.7035 | SCr440 | √ | ||
8620 | 21NiCrMo2 / 1.6523 | SNCM220 |
| ||
8640 | 40NiCrMo2-2 / 1.6546 | SNCM240 |
| ||
-- | 18CrNiMo7-6 / 17CrNiMo6 / 1.6587 | -- |
| ||
9840 | 36CrNiMo4 / 1.6511 | -- |
| ||
E71400 | 41CrAlMo7-10 / 1.8509 | SACM1 |
| ||
-- | 34CrAlNi7 / 1.8550 | -- |
| ||
Bearing Steel | E52100 | 100Cr6 / 1.3505 | SUJ2 | √ | Bearing, Shafts |
-- | 100CrMn6 / 1.3520 | -- |
| ||
-- | 100CrMo7-3 / 1.3536 | -- |
| ||
Spring Steel | 5155 | 55Cr3 / 1.7176 | SUP9 |
| Springs |
6150 | 51CrV4 / 1.8159 | SUP10 |
| ||
9261 | 60CrSi7 / 1.7108 | -- |
| ||
Carbon Steel | 1010 | CK10 / C10E / 1.1121 | S10C |
| Shafts, Chains, Bolts, Nuts, Pins, Suds, Keys, Bites, Came, Couplings etc. |
1020 | C22 / 1.0402 | S20C | √ | ||
1040 | CK40 / C40E / 1.1186 | S40C | √ | ||
1045 | CK45 / C45E / 1.1191 | S45C | √ | ||
1050 | CK50 / C50E / 1.1206 | S50C | √ | ||
1055 | CK55 / C55E / 1.1203 | S55C |
| ||
1064 | CK60 / C60E / 1.1221 | S58C |
| ||
High Speed Tool Steel | M2 | 1.3343 | SKH51 | √ | Reamer, |
M7 | 1.3348 | -- |
| ||
M42 | 1.3247 | SKH59 | √ | ||
M35 | 1.3243 | SKH55 | √ | ||
T1 | 1.3355 | SKH2 |
| ||
T15 | 1.3202 | -- |
| ||
T42 | 1.3207 | SKH57 |
|
Annealing
840 to 870°C
Slow controlled cooling in furnace at a rate of 10 to 20°C/hr down to approx. 600°C, further cooling in air. Hardness after annealing: max. 229 HB.
Stress relieving
Approx. 650°C
Slow cooling in furnace; intended to relieve stresses set up by extensive machining, or in complex shapes. After through heating, hold in neutral atmosphere for 1 - 2 hours.
Hardening
1000 to 1050°C / Oil, air
Holding time after temperature equalization: 15 to 30 minutes.
Obtainable hardness: 53-56 HRC
Tempering
100 to 200°C (212 to 392°F)
Slow heating to tempering temperature immediately after hardening / time in furnace
1 hour for each 20 mm of work piece thickness but at least 2 hours / cooling in air.
For average hardness figures to be obtained please refer to the tempering chart.
What we can offer?
We offer a wide range of steel products in a wide variety of dimensions and executions, acc.to the common international specifications or customerized.
Machining and heat treatment are available.
Also, we advise you in choosing the right materials.
Shape Available
Solid round bar
Flat bar
Square bar
Hexagon bar
Block
Plate
Sheet
Wire rod
Strip
Note:
1). √ means we have stoc.
2). Delivery Condition:
Smelting: EAF+LF+VD (+ESR).
Making: Hot rolled, Cold rolled, Forged, Cold Drawn.
Heat Treatment: Untreated, Annealing, N+T, Q+T.
Surface: Black, Peeled, Turned, Milled, Grinded, Polished.
Q1: What is Ningbo Ningshing Precision Machinery Group Co., Ltd ?
A1: Ningbo Ningshing Precision Machinery Group Co., Ltd., formerly known as Ningbo Ningshing Special-Steel Group Co., Ltd., is the leading distributor of Special Steel, and also a professional mold base maker in China. Our business involves special steel trading, machining processing, mold base making, heat treatment, CNC machines manufacturing.
Q2: Are you a manufacturer or a trader?
A2: For Special Steel, we are the one of the leading distributors and service center in China. 9 warehouses with over 50,000 tons of regular stock. Our workshop has various kinds of equipments for sawing, milling, grinding, drilling etc.
For mold base, we are a professional manufacturer, with 24 sets of CNC machines, 3 axis and 5 axis, CMM for inspection. We produce medium-large sized mold base for plastic injection mold and die casting die.
Q3: How do you control the quality of steels?
A3: Firstly, we have very close and deep relationship with Chinese Prime Mills, choose supplier carefully, and regard them as the long term business partner. Based on the long term cooperation, we concentrate on special steel business and expand the market step by step. Secondly, we have own technical center which is formed by the experienced engineers and technicians whom ever worked for prime mills. We control the quality in production process, in-out warehouse.
Q4:: Which kind of processing can you do?
A4: We do machining processing like cutting, milling, grinding, turning, peeling, drilling, CNC machining. Meanwhile, we do vacuum heat treatment for die and mold.
You Might Also Like
Zinc It Done Water-Based Galvanizing Spray Paint Aqueous Gal......
EPA/Carb Certificated Fuel Line Fuel Hose for Garden Machine......
100g high performance desiccant in Tyvek
Truck Spare Parts Weichai Engine Intake Rocker Arm Best
Art Glass Smoking Water Pipe ( AY 020)
Pdadmac 40% Cationic Polymer for Sludge Dewatering
Hot-Sale HDI Multilayer Printed Circuit Board Fr4 PCB Power ......
High-End Wall Mounted Storage Holder Rack for Kitchen Goldmi......
Rth -1100A Non Woven Sheet Cutting Machine Sheet Label Cutti......
Non Crosslinked Hyaluronic Acid Meso Filler for Lip Injectio......