HDPE Optical Cable Polyethylene Sheath Material Black PE

China HDPE Optical Cable Polyethylene Sheath Material Black PE, Find details about China High-Density Polyethylene, HDPE from HDPE Optical Cable Polyethylene Sheath Material Black PE

Basic Info.

Model NO.

high-density polyethylene

Tensile Strength

22 MPa

Operation Temperature

80 C

Mfr(Melt Flow Rate)

0.2 G/10min

Elongation at Break

680 %

Carbon Black Content

2.53 %

Dielectric Strength

28 Kv/mm

Trademark

JSXD

Transport Package

Aluminum Foil Bag Inside and Kraft Bag Outside

Specification

25 kg

Origin

China

HS Code

3902900090

Model NO.

high-density polyethylene

Tensile Strength

22 MPa

Operation Temperature

80 C

Mfr(Melt Flow Rate)

0.2 G/10min

Elongation at Break

680 %

Carbon Black Content

2.53 %

Dielectric Strength

28 Kv/mm

Trademark

JSXD

Transport Package

Aluminum Foil Bag Inside and Kraft Bag Outside

Specification

25 kg

Origin

China

HS Code

3902900090

Product Desciption

HDPE Optical cable polyethylene sheath material Black PE

Description:
This series of products are suitable for 1KV-10KV aerial cable. Products comply with GB/T15065-2009 standard, with excellent processing performance.

Processing:
This series of products, dry for about 2 hours before processing, drying temperature: 80ºC, drying temperature can rise to 100ºC in the starting state. The processing temperature is suggested to be :180ºC-190ºC-200ºC-200ºC-210ºC-210ºC

Packing:
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag.
Net weight 1000kg: Inner aluminum foil/polyethylene composite film bag, outer polypropylene woven composite bag.

Storage:
The product should be stored in a clean, dry and ventilated warehouse, and should not be damaged by sun, rain, water and other abnormal conditions. Storage temperature should not be lower than 0ºC. The storage period of the product shall not exceed 6 months from the date of production.