Precast Silicone Ab Double Parts Nondeformable Pad Printing Silicone for Electronic Toys RTV Silicon

China Precast Silicone Ab Double Parts Nondeformable Pad Printing Silicone for Electronic Toys RTV Silicon, Find details about China Pad Printing Silicone, Liquid Silicone from Precast Silicone Ab Double Parts Nondeformable Pad Printing Silicone for Electronic Toys RTV Silicon

Model NO.
HY-912 pad silicon
Feature
Liquid
MOQ
1
Trademark
Hong Ye Silicone Rubber
Transport Package
25kg/Drum, 200kg/Drum
Specification
RoHS, MSDS, SGS, ISO9001: 2000
Origin
Shenzhen, China
HS Code
39100000
Model NO.
HY-912 pad silicon
Feature
Liquid
MOQ
1
Trademark
Hong Ye Silicone Rubber
Transport Package
25kg/Drum, 200kg/Drum
Specification
RoHS, MSDS, SGS, ISO9001: 2000
Origin
Shenzhen, China
HS Code
39100000

precast silicone AB double parts nondeformable pad printing silicone for electronic toys rtv silicon
 
 
ModelColorMixing ratio (%)Pot life (mins)Demould
time
( hrs)		hardness( A0 )Tensile-strength (Mpa)Tear-strength (KN/m)Viscosity
(cps)		Shrinkage
rate (%)		Elongation
(%)		   
933# red9: 1303-534±34.8+1/-0.523+2/-210000±2000≤0.1%350~400   
912# white,yellow,any100:3303-516-184.7+1/-0.525+5/-230000±5000≤0.1%310~400   
916# white,yellow,any100:3303-5284.7+1/-0.526+5/-246000±5000≤0.1%510~400   

 
Precast Silicone Ab Double Parts Nondeformable Pad Printing Silicone for Electronic Toys RTV Silicon

Operation instruction for printing pad silicone
1. Wash and clean molds with detergents, dry the molds and use an air gun if necessary, and apply a film of mold release.
 
2. Determine the normal proportion of pad printing silicone and silicone oil on the basis of customer requirements. Add more silicone oils if a larger area of printed pattern and therefore soft rubber head is needed by the customer. Otherwise, add no or less silicone oil for better hardness. For normal pad printing rubber head, hardness between 15 A°--25A°will be appropriate. If excessive amount of silicone oil is added, the number of printing will be limited by an extremely soft rubber head, and the molecular weight of silicone of however supreme quality will be destroyed by silicone oil, and therefore, the phenomenon of compromised resistance to abrasion, solvent and aging.
 
3. The normal proportion is as follows: 100g silicone admixed with 30g silicone oil for a hardness of 20 A° will be suitable for pad printing for alloy toy cars and products with small patterns and contact area. If larger pressure contact surface or soft rubber head is required, the silicone and silicone oil proportion can be adjusted to 100:50, 100:80 and so on. Remember, the more silicone oil is added, the softer the rubber head will be, and the number of pad printing, resistance to abrasion and solvent will be undermined, and hence, heightened cost and more material waste.
 

    4. Admixture amount of curing agent and chemical reaction of silicone: e.g., mix 100g of silicone with 50g of silicone oil, after they are sufficiently and evenly mixed, add curing agent as per 2% of the total weight of silicone and silicone oil, mix again for 2-3 minutes before exhausting. Generally exhausting duration can not exceed 10 minutes; otherwise, the silicone will harden quickly to affect the quality of molding.
 
Precast Silicone Ab Double Parts Nondeformable Pad Printing Silicone for Electronic Toys RTV Silicon

5. Admixture amount of curing agent and silicone reaction:
5.1. Added with 1% of curing agent, silicone can still flow within 2.5 hours, mold can be released in 6-8 hours. 
5.2. Added with 2% of curing agent, silicone can still flow within 50 minutes to 1 hour, mold can be released in 2-3 hours.
5.3. Added with 3% of curing agent, silicone can still flow within 28-30 minutes, mold can be released in 1.5-2 hours 
5.4. Added with 4% of curing agent, silicone can still flow within 10-15 minutes, mold can be released in 1-1.5 hours
5.5. Curing agent reaction rate is related with weather and temperature. Under 25 degree, they can be added according to the instruction or at double amount in winter or under subzero temperature.
(Note: curing agent can not be added above the 4% maximum level and the normal proportion is 2%. If more than 4% is applied, the silicone will condensate too fast for normal usage). 
Above is the mixing data for silicone and curing agent, the precise result of hundreds of times of our experiments. Provided that you arrange production according to our instruction, you are sure to manufacture first class products and maximize your profit - this is not only the need of, but also our responsibility for and a satisfactory answer to our customers. We may not be the first, but we will try to be the best. The customers need is what we pursue !
Precast Silicone Ab Double Parts Nondeformable Pad Printing Silicone for Electronic Toys RTV Silicon








 









Precast Silicone Ab Double Parts Nondeformable Pad Printing Silicone for Electronic Toys RTV Silicon








    

You Might Also Like