China A182-F6nm(UNS S41500, 1.4313, X3CrNiMo13-4)Forged/Forging Blow Out Blowout Preventer RAM Annular dual BOPS Body Bodies Blocks Double Single Triple Bop Body, Find details about China A182-F6nm Forged bop bodies, A182-F6nmForging Parts from A182-F6nm(UNS S41500, 1.4313, X3CrNiMo13-4)Forged/Forging Blow Out Blowout Preventer RAM Annular dual BOPS Body Bodies Blocks Double Single Triple Bop Body
STM A182 is a martensitic stainless steel. The additions of Nickel and Molybdenum, which gives it excellent sub zero notch ductility, superior to other standard 13 Cr, 410 and 420 Mod martensitic stainless steels.
UNS S41500 steel is air hardening, with little danger of thick sections cracking during heat treatment.
In addition to limiting the maximum hardness allowed to 23 HRC max, NACE MR0175 imposes heat treatment temperature restrictions.
The weldability and corrosion resistance of ASTM A182 are also excellent, being extensively used in the manufacture of Valve Bodies, Flanges, Seats, Gates, and Tubulars.
ASTM A182 specifies a minimum 0.2 PS value of 95 KSI. This NACE approved grade is limited to 75 KSI because of the hardness restriction.
| C | Si | Mn | P | S | Cr | Ni | Mo | Fe | |
|---|---|---|---|---|---|---|---|---|---|
| Min | • | • | 0.50 | • | • | 11.50 | 3.50 | 0.50 | 0.00 |
| Max | 0.05 | 0.60 | 1.00 | 0.030 | 0.030 | 14.00 | 5.50 | 1.00 | 0.00 |
Condition: Hardened and Double Tempered
| U.T.S | 95 KSI Min | (655 N/mm2) |
|---|---|---|
| 0.2% Proof Stress | 75 KSI Min | (517 N/mm2) |
| Elongation | 18 % | |
| Red of Area | 35 % | |
| CVN Impacts @ -60°C (-75°F) | 40 Joules |