Alkrothal 720 Resistance Strip for Brake Resistor

China Alkrothal 720 Resistance Strip for Brake Resistor, Find details about China alkrothal 720 strip, alkrothal 720 tape from Alkrothal 720 Resistance Strip for Brake Resistor

Basic Info.

Model NO.

Alkrothal 720

Trademark

TANKII

Specification

RoHs, ISO 9001

Origin

Shanghai, China

HS Code

7506200000

Model NO.

Alkrothal 720

Trademark

TANKII

Specification

RoHs, ISO 9001

Origin

Shanghai, China

HS Code

7506200000

Product Desciption

Alkrothal 720 Resistance Strip for Brake Resistor

Nominal Analysis

Cr	Al	Fe

12.0~15.0	4.0~6.0	Balance

Mechanical Properties

Max Continuous Service Temperature:
Resisivity 20ºC:
Density:
Thermal Conductivity:
Coefficient of Thermal Expansion:
Melting Point:
Elongation:
Micrographic Structure:
Magnetic Property:

950ºC
1.25ohm mm2/m
7.40g/cm3
52.7 KJ/m·h·ºC
15.4×10-6/ºC (20ºC~1000ºC)
1450ºC
Min 16%
Ferrite
magnetic

Size: Thickness 0.01-7mm, width 0.5-1000mm

Surface: BA, 2B

Hardness: Soft, Half hard, hard

Has been used extensively as big power brake resisor and furnace heating elements.

Has less hot strength than Tophet alloys but much higher melting point.

Shanghai TANKII ALLOY MATERIAL Co., Ltd.

FECRAL AND ALCHROME ALLOY PRODUCER IN China, MOST PROFESSIONAL IN THE WORLD

We also produce below grades:

0Cr15Al5 and 0Cr19Al3, etc.

Chemical Composition and Main Property of Fe-Cr-Al Resistance Alloy
Properties \ Grade		1Cr13Al4	0Cr25Al5	0Cr21Al6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
Main Chemical Composition (%)	Cr	12.0-15.0	23.0-26.0	19.0-22.0	22.5-24.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.0	3.0-4.2	5.0-7.0	6.0-7.0
	Re	opportune	opportune	opportune	opportune	opportune	opportune	opportune
	Fe	Bal.	Bal.	Bal.	Bal.	Bal.	Bal.	Bal.
							Nb0.5	Mo1.8-2.2
Max Continuous Service Temperature(oC)		950	1250	1250	1250	1100	1350	1400
Resisivity 20oC (Ωmm2/m)		1.25 ±0.08	1.42 ±0.06	1.42 ±0.07	1.35 ±0.07	1.23 ±0.07	1.45 ±0.07	1.53 ±0.07
Density(g/cm3)		7.4	7.1	7.16	7.25	7.35	7.1	7.1
Thermal Conductivity		52.7	46.1	63.2	60.2	46.9	46.1	45.2
(KJ/m@h@oC)		52.7	46.1	63.2	60.2	46.9	46.1	45.2
Coefficient of Thermal Expansion(α×10-6/oC)		15.4	16	14.7	15	13.5	16	16
Approximate Melting Point( oC)		1450	1500	1500	1500	1500	1510	1520
Tensile Strength(N/mm2)		580-680	630-780	630-780	630-780	600-700	650-800	680-830
Elongation(%)		>16	>12	>12	>12	>12	>12	>10
Section Variation		65-75	60-75	65-75	65-75	65-75	65-75	65-75
Shrink Rate (%)		65-75	60-75	65-75	65-75	65-75	65-75	65-75
Repeatedly Bend Frequency(F/R)		>5	>5	>5	>5	>5	>5	>5
Hardness (H.B.)		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Continuous Service Time		no	≥80/1300	≥80/1300	≥80/1300	≥80/1250	≥50/1350	≥50/1350
Micrographic Structure		Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite
Magnetic Property		Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic