Injection Molding Polyacetal Resin POM Granule with High Quality
China Injection Molding Polyacetal Resin POM Granule with High Quality, Find details about China POM, POM M90 from Injection Molding Polyacetal Resin POM Granule with High Quality
Basic Info.
Plastic Forming Method
Injection
Color
White
Type
Virgin and Recycled
Product
Materials
Trademark
sinopec
Transport Package
25kg/Bag
Specification
COA
Origin
China
HS Code
3907101090
Plastic Forming Method
Injection
Color
White
Type
Virgin and Recycled
Product
Materials
Trademark
sinopec
Transport Package
25kg/Bag
Specification
COA
Origin
China
HS Code
3907101090
Product Desciption
POM:POM/M90/: -->
[] ISO 62 0.7 %
ISO 1183 1.41 g/cm3
ISO 32 0.2 %
190ºC,2.16kg ISO 1133 9 g/10min
23ºC ISO 527 13 %
23ºC ISO 527 50 %
358N,30s ISO 2039 140 MPa
24h,4mm 2.8-2.9
24h,4mm 2.1-2.4
23ºC ISO 527 2700 MPa
23ºC ISO 2039 M82(R114) MPa
23ºC ISO 527 30 %
23ºC ISO 178 61 MPa
ISO 179/1EA 7 KJ/m2
23ºC ISO 527 62 MPa
23ºC ISO 178 2400 MPa
ISO 180/1EA 7.5 KJ/m2
20ºC,50Hz IEC 250 20 ×10-4
21ºC,65%RH ASTM D-495 1.9 mm
20ºC,1KHz IEC 250 10
IEC 93 1015 Ω.cm
20ºC,1KHz IEC 250 3.9
20ºC,1MHz IEC 250 85
IEC 112 600 CTI
20ºC IEC 243 25 KV/mm
20ºC,50Hz IEC 250 3.9
IEC 93 1015 Ω
20ºC,1MHz IEC 250 3.9
21ºC,65%RH IEC 167 7.5 ×10-4Ω
1.8MPa ISO 75 115 ºC
100 ºC
50N ISO 306 B50 150 ºC
20ºC 1.48 J
10N ISO 306 A50 163 ºC
ASTM D-696 11 1×10-5K-1
DSC ISO 3146 172 ºC
UL 94(FMVSS) HB(B50)
| Item | Test data | Data unit | Test method |
| Water Absorption | 0.7 | % | ISO62 |
| Density | 1.41 | g/cm3 | ISO1183 |
| MFI(190ºC,2.16kg) | 27 | g/10min | ISO1133 |
| Contractility Injection (flow direction) | 2.5-2.7 | ||
| Contractility Injection (vertical) | 2.0-2.2 | ||
| Yield elongation | 8 | % | ISO527 |
| Elongation at break | 20-30 | % | ISO527 |
| Tensile modulus | 3000 | Mpa | ISO527 |
| Bending strength | 68 | Mpa | ISO178 |
| Tensile yield strength | 65 | Mpa | ISO527 |
| Flexural modulus | 2600 | Mpa | ISO178 |
| Item | Test data | Data unit | Test method |
| Water Absorption | 0.7 | % | ISO62 |
| Density | 1.41 | g/cm3 | ISO1183 |
| MFI(190ºC,2.16kg) | 27 | g/10min | ISO1133 |
| Contractility Injection (flow direction) | 2.5-2.7 | ||
| Contractility Injection (vertical) | 2.0-2.2 | ||
| Yield elongation | 8 | % | ISO527 |
| Elongation at break | 20-30 | % | ISO527 |
| Tensile modulus | 3000 | Mpa | ISO527 |
| Bending strength | 68 | Mpa | ISO178 |
| Tensile yield strength | 65 | Mpa | ISO527 |
| Flexural modulus | 2600 | Mpa | ISO178 |
You Might Also Like
Zinc It Done Water-Based Galvanizing Spray Paint Aqueous Gal......
EPA/Carb Certificated Fuel Line Fuel Hose for Garden Machine......
100g high performance desiccant in Tyvek
Truck Spare Parts Weichai Engine Intake Rocker Arm Best
Art Glass Smoking Water Pipe ( AY 020)
Pdadmac 40% Cationic Polymer for Sludge Dewatering
Hot-Sale HDI Multilayer Printed Circuit Board Fr4 PCB Power ......
High-End Wall Mounted Storage Holder Rack for Kitchen Goldmi......
Rth -1100A Non Woven Sheet Cutting Machine Sheet Label Cutti......
Non Crosslinked Hyaluronic Acid Meso Filler for Lip Injectio......