1.3247/M42 High Speed Special Steel Product

China 1.3247/M42 High Speed Special Steel Product, Find details about China Mould Steel, High Speed Steel from 1.3247/M42 High Speed Special Steel Product

Basic Info.

Model NO.

1.3247, M42, SKH59, W2Mo9Cr4VCo8

Special Use

Used for Cutter in Common Use

Application

Tool Steel Bar

The Epidermis

Black or Silver Material

Thickness

5mm-800mm

Length

100mm-5800mm

Width

50mm-22000mm

Grade

1.3247, M42, Skh59, W2mo9cr4vco8

Annealed Hardness

255hbs

Certificate

ISO / Mill Certificate

Test

SGS / Ut 100% / Element Testing

Payment

30% Deposit, Blance by L/C at Sight or T/T

Delivery Quantity

Include MOQ

Trademark

CF STEEL

Transport Package

Export Standard Packing or Customers′demand

Specification

DIN JIS AISI GB

Origin

China

HS Code

7225

Model NO.

1.3247, M42, SKH59, W2Mo9Cr4VCo8

Special Use

Used for Cutter in Common Use

Application

Tool Steel Bar

The Epidermis

Black or Silver Material

Thickness

5mm-800mm

Length

100mm-5800mm

Width

50mm-22000mm

Grade

1.3247, M42, Skh59, W2mo9cr4vco8

Annealed Hardness

255hbs

Certificate

ISO / Mill Certificate

Test

SGS / Ut 100% / Element Testing

Payment

30% Deposit, Blance by L/C at Sight or T/T

Delivery Quantity

Include MOQ

Trademark

CF STEEL

Transport Package

Export Standard Packing or Customers′demand

Specification

DIN JIS AISI GB

Origin

China

HS Code

7225

Product Desciption

1.3247/M42 High Speed Special Steel Product

Application:
Used for cutters in common use.
1) This for high speed steel, tungsten steel adaptable to make strong cutting use wear-resisting, resistance to impact a variety of tools, advanced punching die, screw die;
2) Is need toughness and shape complex tools, milling cutter, drill, etc

Feature:
1)Die steel for manufacturing strong cutting with wear-resistant, resistant to impact a variety of tools;
2)Specially for hard and hi-speed cutting;

Preheat temperature: 730-730 °C

Quenching temperature: 1190-1210 °C

Tempering temperature:Cold drawn, hardness 285 HBS,Cold drawn after annealing condition, hardness 277 HBS;

Heat treatment
Fire: isothermal annealing temperature is 800 ~ 880 °C, with 10 ~ 20 °C, the dHr furnace cooling to about 600 °C, hardness above HB269;

Chemical composition(%)

C	Si	Mn	P	S	Cr	V	W	Mo	Co
1.~1.15	≥0.65	≥0.40	≤0.030	≤0.030	3.50~4.50	0.95~1.35	1.15~1.85	9.0~10.0	7.50~8.50

Quenching methods: oil quenching, air cooling or salt bath quenching;

Delivery state: forging parts produced with continuous casting and electro-slag re-melting process; rolled as annealed, bright and quenched/tempered steel bars.

Listed specifications are only typical grades; products of required specifications can be developed/produced per international, Chinese or industry standards, or based on agreements with customers.

Packing: Export Standard Packing or Customers'demand;