China Fiberglass Woven Roving for Hand Lay up, Find details about China Fiberglass Woven Roving, Fiberglass Fabric from Fiberglass Woven Roving for Hand Lay up
Fiberglass woven roving are bidirectional fabric made by interweaving direct rovings. Can be compatible with unsaturated polyester, vinyl ester, epoxy and phenolic resins. With high-performance reinforcement. Widely used in hand lay up and robot processes to manufacture boats, vessels, plane and automotive parts, furniture and sports facilities.
The area weight is from 200g/m2 to 1200g/m2, the width is from 50mm-3000mm.
Fiberglass woven roving are commonly used in all types of FRP construction applications. Sometimes referred to as boat cloth, there is a wide variety of weights available to suit your needs.
Clean woven surface,even thickness,no fuzz.
Good molding property,easily delete air bubbles and quickly wet out(resin).
Final products are with high mechanical strength,efficiently retain mechanical strength against bolled warer.
ITEM | STANDARD VALUE | STANDARD NO | ||
Weight(g/m2) | 800±64 | GB/T9914.3 | ||
Breaking strength N/2.5cm | Warp | ≥4800 | GB7689.5 | |
Weft | ≥4400 | GB7689.5 | ||
Binder content (%) | 0.4-0.8 | GB9914.2 | ||
Moisture content (%) | <0.2 | GB11966 | ||
Density | Warp | 2.0±0.3 | GB7689.6 | |
Weft | 1.8±0.4 | GB7689.6 |
Each roll put into a polyethylene bag,fastened the bag entrance and packed into a suitable cardboard box or plastic bag upon to customer's request,this product could be shipped either with carton packaging only or with pallet packaging. In pallet packaging,the products could be horizontally put on the pallets and fastened with packing straps and shrink film.
This product should be stocked in dry and cool places.The best condition is with temperature between 5ºC and 35ºC,with a relative humidity between 35% and 65%.Please keep the product in its original packaging before use,avoiding moisture.