Haiteng Customized Delrin/ POM Machine Parts by CNC Lathe Machine
China Haiteng Customized Delrin/POM Machine Parts by CNC Lathe Machine, Find details about China Pure PTFE Gasket, Teflon PTFE Plastic Part from Haiteng Customized Delrin/POM Machine Parts by CNC Lathe Machine
Basic Info.
Model NO.
POM Part
Customized
as Drawings or Samples
Trademark
HAITENG
Transport Package
Wooden Box with Foam Lined in Safe Conditions
Specification
Customized
Origin
Yangzhong China
HS Code
3920109090
Model NO.
POM Part
Customized
as Drawings or Samples
Trademark
HAITENG
Transport Package
Wooden Box with Foam Lined in Safe Conditions
Specification
Customized
Origin
Yangzhong China
HS Code
3920109090
Product Desciption
HAITENG Customized Delrin/POM Machine Parts by CNC Lathe Machine
Characteristics
-High surface hardness
-Good wear resistance
-Excellent machinability
-Nice self-lubricating properties
-Good dimensional stability
-Low water absorption
-Oil resistant
-Work under the temperature of -40-100ºC
Images
The common document files accepted are : *.pdf/*.dwg/*.IGS/*.step/*.prt/*.sldprt Just send the drawings to us, we will handle the rest for you.
Technical data sheet
The machining process include below
1.Turning: For parts which have high surface requirement, wide-head cutters are better. When processing thin walled and soft material, cutters like knife are recommended.
2. Milling: When milling the surface, end-milling is more cost-effective than circular milling. For circular and forming cutter, it should have less than two cutter edges. In this case, the tolerance caused due to the edge vibration can be lowered to the minimum.
3. Sawing: Thin saws are usually used to saw thick parts to avoid the heating caused by friction. It would be better to use sharp and big sawblade.
4. Drilling: When drilling the solid materials, make sure to use sharp drill, otherwise the increasing pressure during drilling will cause material cracks.
The common document files accepted are : *.pdf/*.dwg/*.IGS/*.step/*.prt/*.sldprt Just send the drawings to us, we will handle the rest for you.
Characteristics
-High surface hardness
-Good wear resistance
-Excellent machinability
-Nice self-lubricating properties
-Good dimensional stability
-Low water absorption
-Oil resistant
-Work under the temperature of -40-100ºC
Images
The common document files accepted are : *.pdf/*.dwg/*.IGS/*.step/*.prt/*.sldprt Just send the drawings to us, we will handle the rest for you.
Technical data sheet
| PROPERTIES | Unit | Value |
| I.Physical Properties | ||
| Density | g/cm3 | 1.45 |
| Water absorption 24hrs | % | < 0.3 |
| II.Thermal Properties | ||
| Heat deflection temperature - HDT/A | ºC | 110 |
| Min. service temperature | ºC | -40 |
| Max. service temperature | ºC | 100 |
| Thermal conductivity at 23 ºC | W/(K*m) | 0.31 |
| Coefficient of linear thermal expansion | 10-4*K-1 | 1.2 |
| Flammability Rating(6mm thickness) | - | HB |
| III.Mechanical Properties at 23ºC | ||
| Tensile strength at yield | MPa | 63 |
| Tensile strength at break | Mpa | - |
| Elongation at break | % | 31 |
| Modulus of elasticity after tensile test | MPa | 2,700 |
| Modulus of elasticity after flexural test | MPa | - |
| Hardness - Shore D | 83 | |
| Charpy impact strength | kJ/m2 | N. B. |
| Friction coefficient | 0.35 | |
| IV.Electrical Properties at 23ºC | ||
| Dielectric constant at 1 MHz | 106Hz | 3.8 |
| Dielectric loss factor at 1 MHz | 106Hz | 0.005 |
| Volume resistively | Ohm (Ω) * cm | >1013 |
| Surface resisively | Ohm (Ω) | >1013 |
| Dielectric strength | kV/mm | 40 |
The machining process include below
1.Turning: For parts which have high surface requirement, wide-head cutters are better. When processing thin walled and soft material, cutters like knife are recommended.
2. Milling: When milling the surface, end-milling is more cost-effective than circular milling. For circular and forming cutter, it should have less than two cutter edges. In this case, the tolerance caused due to the edge vibration can be lowered to the minimum.
3. Sawing: Thin saws are usually used to saw thick parts to avoid the heating caused by friction. It would be better to use sharp and big sawblade.
4. Drilling: When drilling the solid materials, make sure to use sharp drill, otherwise the increasing pressure during drilling will cause material cracks.
The common document files accepted are : *.pdf/*.dwg/*.IGS/*.step/*.prt/*.sldprt Just send the drawings to us, we will handle the rest for you.
You Might Also Like
Zinc It Done Water-Based Galvanizing Spray Paint Aqueous Gal......
EPA/Carb Certificated Fuel Line Fuel Hose for Garden Machine......
100g high performance desiccant in Tyvek
Truck Spare Parts Weichai Engine Intake Rocker Arm Best
Art Glass Smoking Water Pipe ( AY 020)
Pdadmac 40% Cationic Polymer for Sludge Dewatering
Hot-Sale HDI Multilayer Printed Circuit Board Fr4 PCB Power ......
High-End Wall Mounted Storage Holder Rack for Kitchen Goldmi......
Rth -1100A Non Woven Sheet Cutting Machine Sheet Label Cutti......
Non Crosslinked Hyaluronic Acid Meso Filler for Lip Injectio......