China Professional Manufacturer Oil Resistant Polyolefin Made Heat Shrink Tubing, Find details about China 150 Degrees Heat Shrink Tube, High Temperature Resistant Tube from Professional Manufacturer Oil Resistant Polyolefin Made Heat Shrink Tubing
| Item | CL-DR |
| Continuus Temperature Range | -55ºC~150ºC |
| Radial Shrinking Ratio | 2:1 |
| Longitudinal Shrinking Ratio | ±10% |
| Dielectric Voltage Withstand | 600V |
| Environmental standards | ROHS REACH |
| Color | Black |
| Flammability | VW-1 |
| Performance Testing | Test Methods | Performance indicators | ||
| Tensile Strength(MPa) | ASTM D2671 | ≥13.8 | ||
| Elongation Ratio(%) | ASTM D2671 | ≥300% | ||
| Tensile Strength(MPa) | ASTM D2671(150ºC/168h) | ≥10.3 | ||
| Elongation Ratio(%) | ASTM D2671 (150ºC/168h) | ≥300% | ||
| Fluid resistance | 0#Diesel | Tensile Strength(MPa) | ASTM D2671 (23ºC/24h) | ≥10.3 |
| Elongation Ratio(%) | ≥300% | |||
| Weight gain ratio | <=15% | |||
| IRM902 | Tensile Strength(MPa) | UL-224 70ºC/4h , | Retention rate≥75% | |
| Elongation Ratio(%) | Retention rate≥75% | |||
| Weight gain ratio | <=15% | |||
| IRM903 | Tensile Strength(MPa) | ASTM D2671 (70ºC/ 24h) | ≥10.3 | |
| Elongation Ratio(%) | ≥300% | |||
| Weight gain ratio | <=20% | |||
| Copper corrosion | Copper corrosion | ASTM D2671(150°C/168) | No brittleness, glass tube or crack; no pitting copper | |
| Elongation Ratio(%) | ≥200% | |||
| Size | supplied(mm) | After heating(mm) | Package | |
| min ID (Inside Diameter) | Max ID (Inside Diameter) | T(Wall-thickness) | (Meter/Roll) | |
| Φ3.2 /1.6 | 3.2 | 1.6 | 0.76±0.15 | 100 |
| Φ4.8/2.4 | 4.8 | 2.4 | 0.85±0.15 | 100 |
| Φ6.4/3.2 | 6.4 | 3.2 | 0.89±0.15 | 100 |
| Φ9.5/4.8 | 9.5 | 4.8 | 1.02±0.20 | 50 |
| Φ12.7/6.4 | 12.7 | 6.4 | 1.22±0.20 | 50 |
| Φ19.1/9.5 | 19.1 | 9.5 | 1.45±0.28 | 50 |
| Φ25.4/12.7 | 25.4 | 12.7 | 1.78±0.28 | 25 |
| Φ38.1/19.0 | 38.1 | 19 | 2.41±0.41 | 25 |
| Φ50.8/25.4 | 50.8 | 25.4 | 2.79±0.41 | 20 |
| Remarks: Special specifications, sizes and special packaging requirements can be customized according to customer requirements. | ||||